采用热分解法制备了钛基二氧化锡电极,并用XRD,SEM对电极涂层进行了表征,应用快速电极寿命法测试了钛基二氧化锡电极在60℃,1.0 mol/L H2SO4溶液中的使用寿命.以降解苯酚为目标,用循环伏安法考察了该电极的电催化氧化性能.结果表明,苯酚转化率达到96.5%,其电催化性能优于传统单质铅电极和Ti/PbO2电极,是1种优良的电催化剂.
参考文献
| [1] | Trasatti S .[J].Electrochim Aeta,1984,29(11):1503. |
| [2] | Wang Fan et al.[J].Journal of Electroanatytical Chemistry,2001,510(1～2):29. |
| [3] | Gennaro Armando et al.[J].Electrochemistry Communications,2004,6(07):627. |
| [4] | Krysa Josef et al.[J].Electrochimica Acta,1995,40(12):1997. |
| [5] | Manoharan R et al.[J].Journal of Power Sources,1997,66(1～2):155. |
| [6] | Kamachi Mudali U et al.[J].JOURNAL OF NUCLEAR MATERIALS,2000,277(01):49. |
| [7] | Devilliers D et al.[J].Electrochimica Acta,2004,49(14):2369. |
| [8] | Chang Jeng-Kuei et al.[J].Electrochemistry Communications,2004,6(07):666. |
| [9] | Prasad Kalakodimi Rajendra et al.[J].Journal of Power Sources,2004,135(1-2):354. |
| [10] | Correa Lozano B.[J].JOURNAL OF APPLIED ELECTROCHEMISTRY,1997(27):970. |
| [11] | 张招贤,郑团.涂层钛阳极强化寿命试验电解因素的选择[J].氯碱工业,2004(05):10-11. |
| [12] | Chiaki Iwakura;Meguru Inai;Masatsugu Manabe .[J].电化学すょひ工业物理化学,1980,48(02):91. |
| [13] | 王雅琼,童宏扬,许文林.Sno2+Sb203中间层的制备条件对Ti/SnO2+Sb2O3/PbO2阳极性能的影响[J].应用化学,2004(05):437-441. |
| [14] | 阎建中,曲久辉,孙志民,李梅,刘瑞平.热处理对SnO2/Ti电化学催化降解p-苯醌的影响[J].环境科学,2004(01):30-34. |
| [15] | 王静,冯玉杰.制备方法对稀土Gd掺杂SnO2/Sb电催化电极性能的影响[J].吉林大学学报（理学版）,2005(04):546-550. |
| [16] | 梁镇海,孙彦平.Ti/SnO2+Sb2O3+MnO2/PbO2阳极的性能研究[J].无机材料学报,2001(01):183-187. |
| [17] | Gattrell M;Kirk D W .[J].Journal of the Electrochemical Society,1993,140(06):1534. |
| [18] | Kotz R;Stucki S;Career B .[J].Journal of Applied Electrochemistry,1991,21(01):14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%