利用“溶液共混-挤出交联-冷冻干燥”法制备了基于海藻酸钙-聚乙烯醇(PVA)共混物的离子响应型泪道栓子,研究了PVA用量对共混材料体积膨胀率、吸水率及降解性能的影响.结果显示,在模拟泪液中,各共混材料的膨胀速率均与时间成线性关系,膨胀速率随着PVA用量的增加而逐渐降低,膨胀曲线斜率从66.53降至10以下.另外,随着PVA用量的增加,共混材料的吸水率以及降解过程中的质量保留率均先减少后增大,分别当PVA用量为20%时达到最小.
参考文献
[1] | Olivas G. I.;Barbosa-Canovas G. V. .Alginate-calcium films: water vapor permeability and mechanical properties as affected by plasticizer and relative humidity.[J].LWT-Food Science & Technology,2008(2):359-366. |
[2] | Kuo CK;Ma PX .Ionically crosslinked alginate hydrogels as scaffolds for tissue engineering: part 1. Structure, gelation rate and mechanical properties.[J].Biomaterials,2001(6):511-521. |
[3] | Ji-Won Rhim;Ho Bum Park;Choong-Sub Lee;Ji-Hyun Jun;Dae Sik Kim;Young Moo Lee .Crosslinked poly(vinyl alcohol) membranes containing sulfonic acid group: proton and methanol transport through membranes[J].Journal of Membrane Science,2004(1/2):143-151. |
[4] | 潘育松,熊党生,陈晓林.聚乙烯醇水凝胶的制备及性能[J].高分子材料科学与工程,2007(06):228-231. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%