钒氮钢中铁素体等温形核规律的试验研究

钢铁, 2005, 40(10): 63-67.

1.钢铁研究总院结构材料研究所,北京,100081

2.钢铁研究总院结构材料研究所,北京,100081

3.钢铁研究总院结构材料研究所,北京,100081

Effect of V(C,N) Precipitated in Austenite on Ferrite Nucleation in V-N Steel

采用Geeble 3500热模拟试验机,对比研究了钒氮钢、钒钢的等温相变特征.结果表明,在相变过程中,钒氮钢中铁素体形核总量和晶内铁素体形核数量都明显高于钒钢,分析认为,这与钒氮钢中V(C,N)的析出造成了铁素体形核位置的改变,同时也增加了形核位置密度有关,尝试用一种新的形核方式对此进行了描述.

[1]	Swedish Institute of Metals Research .Grain Refinement by Intragranular Ferrite Nucleation in V-N Steels[R].2nd Progress Report for VANITEC,Stockholm,2001.
[2]	龚维幂,杨才福,张永权,王青峰.低碳钒氮微合金钢中V（C,N）在奥氏体中的析出动力学[J].钢铁研究学报,2004(06):41-46.
[3]	大森章夫 .Effet of VN Precipitates on Formation of Grain Boundary and Intragranular Ferrite in a High N-V Bearing Steel[J].铁と钢(日本),1998,84(11):35-41.
[4]	Zhang S H;Hattori N;Enomoto M et al.Ferrite Nucleation at Ceramic/Austenite Interfaces[J].ISIJ International,1996,36:1301.
[5]	Yang ZG.;Enomoto M. .A discrete lattice plane analysis of coherent f.c.c./B1 interfacial energy[J].Acta materialia,1999(18):4515-4524.
[6]	J.-H. SHIM;Y. W. CHO .NUCLEATION OF INTRAGRANULAR FERRITE AT Ti2O3 PARTICLE IN LOW CARBON STEEL[J].Acta materialia,1999(9):2751-2760.
[7]	潘涛,杨志刚,白秉哲,方鸿生.钢中夹杂物与奥氏体基体热膨胀系数差异导致的热应力和应变能研究[J].金属学报,2003(10):1037-1042.
[8]	付俊岩;孟繁茂.高钒氮微合金化钢的物理冶金及其应用[A].,2000:2.
[9]	森影康;大井健次;川端文丸 .低碳素鋼にぉけるTiN上のフェラィト核生成に及ばすTiNサィズの影響[J].铁と钢(日本),1998,84:40-45.

上一张下一张

计量

作者相关

文章评分