根据管材现场服役环境、受力及腐蚀工况,设计出了能真实反映现场条件的新型高温高压釜以及适用于高温高压环境开裂的恒载荷实验夹具.结果表明,高温高压80％σs应力腐蚀实验后C110管材抗拉强度、屈服强度降低幅度分别达到4.7％和5.0％,出现明显套损现象,为油气田管材适用性评价和高温高压损伤失效提供新方法.
参考文献
| [1] | Kopliku A,Tabinor M,Ryder J,et al.High strength modified martensitic stainless steel production tubing for sour wells[A].Corrosion 2009[C].Atlanta,GA:NACE,2009 |
| [2] | Kermani M B,Harrop D,Truchon M L,et al.Experimental limits of sour service for tubular steels[A].Corrosion 1991[C].Houston,TX:NACE 1991 |
| [3] | Nice R I,MartinJ W.Application limits for super martensitic and precipitation hardened stainless steel bar-stock materials[A].Corrosion 2005[C].Houston,TX:NACE,2005 |
| [4] | Morana R,Nice R I.Corrosion assement of high strength carbon steel grades P-110,Q-125,140 and 150 for H2S containing producing well environments[A].Corrosion 2009[C].Atlanta,GA:NACE,2009 |
| [5] | Cemocky E P,Aaron V D,Paslay P R,et al.Combined axial Tension/Compression and Internal Pressure Testing of mini-pipe Specimens in H2S environment to determine three dimensional(Triaxial)stress states which produce crack initiation failure:explanation of the new test fixture,mini-pipe specimen,and preliminary test results[A].SPE2005[C].The Woodlands,Texas:SPE,2005 |
| [6] | 吴介卿.由简单拉伸试验测定延性金属断裂韧性K1c[P].中国,90101158,1991 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%