采用复合化学镀方法在铝合金微弧氧化陶瓷膜表面制备了Ni-P-SiC复合镀层,研究了镀液中SiC浓度对复合镀层物相、显微组织、沉积速率的影响,并测试了复合涂层(陶瓷J/复合镀层)的结合力.结果表明:Ni-P-SiC复合镀层为非晶态结构,与陶瓷膜的界面清晰,完全封闭了微弧氧化陶瓷膜表面的微孔;随着镀液中SiC含量的增加,复合镀层沉积速率降低,SiC共析量则是先快速增大,当含量达到16 g/L后就基本保持不变.
参考文献
| [1] | MUKHOPADHYAY A K .High Strength Aluminum Alloys for Structural Application[J].Metals Materials and Processes,2007,119(01):1-6. |
| [2] | CHEN K H;LIU H W;ZHANG Z et al.The Improvement of Constituent Dissolution and Mechanical Properties of 7055 Aluminum Alloy by Stepped Hcat Treatments[J].Journal of Materials Processing Technology,2003,142:190-196. |
| [3] | 刘晓涛,董杰,崔建忠,赵刚.高强铝合金均匀化热处理[J].中国有色金属学报,2003(04):909-913. |
| [4] | 李忠盛,吴护林,潘复生,张隆平,何庆兵.氧化时间对7A55铝合金微弧氧化膜的影响[J].航空材料学报,2009(03):23-26. |
| [5] | Yerokhin AL;Shatrov A;Samsonov V;Shashkov P;Pilkington A;Leyland A;Matthews A .Oxide ceramic coatings on aluminium alloys produced by a pulsed bipolar plasma electrolytic oxidation process[J].Surface & Coatings Technology,2005(2/3):150-157. |
| [6] | 吴振东,姜兆华,姚忠平,孙学通,张雪林.纯铝及其合金的微等离子体氧化成膜特征[J].中国有色金属学报,2005(06):946-951. |
| [7] | 方信贤.中温酸性化学镀镍磷合金组织和性能研究[J].表面技术,2007(04):25-27. |
| [8] | RIEDEL W.Electroless Nikel Plating[M].UK:Fingshing Publications Ltd,1991 |
| [9] | 李忠盛,吴护林,潘复生,张隆平,何庆兵.7A55铝合金微弧氧化陶瓷膜的组织与性能[J].航空材料学报,2010(05):54-57. |
| [10] | 刘元,李兴俊,龚正朋.氧化时间对7A09超高强铝合金微弧氧化陶瓷膜的影响[J].表面技术,2013(02):53-55,73. |
| [11] | 陈月华,刘永永,江德凤,袁礼华.化学镀镍施镀过程稳定性分析[J].表面技术,2013(02):74-76. |
| [12] | 范雄.X射线金属学[M].北京:机械工业出版社,1998:103-104. |
| [13] | BALARAJU J N;EZHILSELVI V;WILLIAM V K .Electro Chemical Studies on Electroless Ternary and Quaternary Ni-P Based Alloy[J].Electro Chemical Acta,2006,52:1064-1074. |
| [14] | 阳范文,赵耀明,高茜斐.表面活性剂对Ni-P-SiC化学复合镀层性能的影响[J].材料保护,2000(09):12-13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%