通过微弧氧化法(MAO)在表面预氧化镍钛(NiTi)丝(直径(0)0.5mm)表面制备含Ca、P的均匀微孔涂层,对不同处理时间形成的涂层进行扫描电镜(SEM)形貌观察和电子探针(EPMA)成分分析,并探查了涂层的血液相容性.实验结果表明,表面预氧化的NiTi丝在微弧氧化处理时,随微弧氧化时间的延长,氧化层中Ti/Ni提高,Ca、P含量也提高.微弧氧化20s时,涂层质量较好,微孔均匀分布,微孔孔径1μm左右,表面没有裂纹,而且此时涂层有较好的生物相容性.
参考文献
| [1] | Bansiddhi,A;Sargeant,TD;Stupp,SI;Dunand,DC .Porous NiTi for bone implants: A review.[J].Acta Biomaterialia,2008(4):773-782. |
| [2] | Shevchenko N;Pham MT;Maitz MF .Studies of surface modified NiTi alloy[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2004(1/2):126-131. |
| [3] | Troczynski Tomasz;Liu Deannlo et al.[P].USI 6730324,2004-04-05. |
| [4] | Shabalovskaya S;Anderegg J;Van Humbeeck J .Critical overview of Nitinol surfaces and their modifications for medical applications.[J].Acta biomaterialia,2008(3):447-467. |
| [5] | Sun Jifeng;Han Yong;Huang Xin .[J].Surface ＆ Coat-ings Technology,2007,201:5655-5658. |
| [6] | 刘福,徐吉林,王福平,赵连城,孙德智.医用NiTi合金的表面改性研究进展[J].稀有金属材料与工程,2008(04):748-752. |
| [7] | Xu J L;Liu F;Wang F P et al.[J].Materials Letters,2008,62(25):4112-4114. |
| [8] | Xu C H;Ma X Q;Shi S Q et al.[J].Materials Seience and Engineering A,2004,371:45-50. |
| [9] | 肖萍,郑少波,尤静林,蒋国昌,陈辉,曾昊.钛氧化物结构及其拉曼光谱表征[J].光谱学与光谱分析,2007(05):936-939. |
| [10] | Armitage DA.;Grant DM. .Characterisation of surface-modified nickel titanium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):89-97. |
| [11] | 崔福斋;冯庆玲.生物材料血[M].北京:清华大学出版社,2004:244. |
| [12] | Plant S D;Grant D M et al.[J].Materials Letters,2007,61:2864-2867. |
| [13] | 杨贤金,崔振铎,赵乃勤,宋文静,曾晟宇,朱胜利,姚康德.Ca/P层对NiTi形状记忆合金生物相容性的影响[J].材料研究学报,2000(05):481-484. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%