Ti(C, N)-based cermets were treated using hot isostatic pressing (HIP) at 1423 K in nitrogen. The microstructures compared with the as-sintered cermets were investigated using X-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray analysis, and electron microprobe analysis. It was found that high nitrogen activity in the surface zone resulted in the formation of gradient structure. Approximately 20-μm-deep, nitrogen-rich and titanium-rich hard surface zone was introduced by the beat treatment. The nitrogen activity was the driving force that caused the transportation of the atoms through the binder, titanium towards the surface, and tungsten and molybdenum inwards. In the surface zone, the particle size became fine, the inner rim disappeared, and the volume fraction of the outer rim and the binder phase considerably reduced. Small grains of TiN, WC, Mo2C, and nitrogen-rich carbonitride phases formed in the surface zone during the heat treatment, improving the tribological property of the heat-treated cermet.
参考文献
| [1] | 郑勇,熊惟皓,游敏,刘文俊.Microstructural evolution and characteristics during sintering of submicron Ti(C,N)-based cermet[J].中国有色金属学会会刊(英文版),2003(06):1424-1429. |
| [2] | Lindahl P;Rosen A E;Gustafson P;Rolander U, Andren H.O .Effect of pre-alloyed raw materials on the microstructure of a (Ti,W)(C,N)-Co cermet[J].International Journal of Refractory Metals and Hard Materials,2000,18:273. |
| [3] | Zackrisson J;Andren H O .Effect of carbon content on the microstructure and mechanical properties of (Ti,W,Ta,Mo)(C,N)-(Co,Ni) cermets[J].International Journal of Refractory Metals and Hard Materials,1999,17:265. |
| [4] | Zheng Y;Xiong W H;Liu W J;Lei W, Yuan Q .Effect of nano addition on the microstructures and mechanical properties of Ti(C,N)-based cermets[J].Ceramics International,2005,31:165. |
| [5] | Stefano Piscanec;Lucio Colombi;Erik Vesselli;Giovanni Comelli;Orfeo Sbaizero;Sergio Meriani;Alessandro De Vita .Bioactivity of TiN-coated titanium implants[J].Acta materialia,2004(5):1237-1245. |
| [6] | Sung H K;Young J B;Dongil K .Analysis of interfacial strengthening from composite hardness of TiN/VN and TiN/NbN multilayer hard coatings[J].Surface and Coatings Technology,2004,187:47. |
| [7] | Bhowmick S.;Kale AN.;Jayaram V.;Biswas SK. .Contact damage in TiN coatings on steel[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2003(2):250-258. |
| [8] | Walter Lengauer;Klaus Dreyer .Functionally graded hardmetals[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):194-212. |
| [9] | Frykholm R.;Andren HO. .Development of the microstructure during gradient sintering of a cemented carbide[J].Materials Chemistry and Physics,2001(1/3):203-208. |
| [10] | Park Y J;Kim S W;Kang S .The formation of a solid solution band at the surface of Ti(C,N)-based cermets[J].Materials Science and Engineering,2000,291A:198. |
| [11] | Atkinson H V;Davies S .Fundamental aspects of hot isostatic pressing:an overview[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000,31:2981. |
| [12] | Sabatello S;Frage N;Dariel M P .Graded TiC-based cermets[J].Materials Science and Engineering,2000,288A:12. |
| [13] | Limin C;Walter L;Klaus D .Advances in modern nitrogen-containing hardmetals and cermets[J].International Journal of Refractory Metals and Hard Materials,2000,18:153. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%