采用超声脉冲电解法从含铜电镀废液中回收铜粉,系统研究了电流密度、占空比、脉冲频率、温度、超声功率等因素对铜粉回收率和剩余铜离子浓度的影响,并采用SEM、XRD等对所回收的铜粉进行表征.研究结果表明,各因素对铜离子回收率影响规律不同;较优的铜粉回收工艺为:电流密度1000A/m~2、占空比50%、脉冲频率1000Hz、温度40℃、超声功率640W,在此工艺下铜离子的回收率达98.75%,所回收的铜粉呈枝晶状;加入表面活性剂十二烷基苯磺酸钠可使铜粉从枝晶状转变为类球状.

Ultrasonic pulse electrolysis is proposed to recover copper from the copper-containing electroplating effluent.The influences of current density,duty cycle,pulse frequency,temperature and ultrasonic power on the recovery rate and residual concentration of Cu~(2+) are systematically studied.The recovery copper powders are characterized by SEM and XRD.The results show that the effects of various factors on the recovery rate of Cu~(2+) are different.The optimum recovery process is recommended as follows:current density is 1000A/m~2,duty cycle is 50%,pulse frequency is 1000Hz,temperature is 40 ℃ and ultrasonic power is 640W,under this process the recovery rate of Cu~(2+) is 98.75% and the recovery copper powder is dendritical The addition of SDBS can make the morphology of ultrafine copper powder from the dendrite shape into near-spherical shape.

参考文献

[1] 陈维平,王眉,杨超,李元元.电解方法制备纳米金属粉末的研究进展[J].材料导报,2007(12):79-82.
[2] 郭仁东,吴昊,张晓颖.高浓度含铜废水处理方法的研究[J].当代化工,2004(05):280-281,310.
[3] 鲁道荣,何建波,李学良,朱云贵,杨馨.高电流密度脉冲电解制备纯铜的研究[J].有色金属(冶炼部分),2002(05):11-14.
[4] 安成强;崔作兴;郝建军.电镀三废治理技术[M].北京:国防工业出版社,2003:139.
[5] 王菊香,赵恂,潘进,尹新方.超声电解法制备超细金属粉的研究[J].材料科学与工程,2000(04):70-74.
[6] 张少峰 .三维电极电沉积去除废水中重金属铅和镍[D].北京:清华大学,2003.
[7] 许文林,李敏,傅相林,王雅琼.超声功率对电化学沉积铜过程速率的影响[J].应用声学,2007(02):125-封3.
[8] 徐瑞东,常仕英,郭忠诚.电解法制备超细铜粉的工艺及性能研究[J].电子工艺技术,2006(06):355-359.
[9] 李淼,喻建胜,蒋渝,陈家钊,涂铭旌.超声电沉积制备纳米铜粉末的机理研究[J].材料开发与应用,2004(03):12-15.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%