采用以铁精粉、煤粉和石灰石为主要原料制成含碳球团,在1 573、1 623、1 673K下进行了不同加热时间的还原试验研究,并分析计算了炉料带入硫的去向。试验结果表明：在温度为1 673K、12min时,渣铁已经能够很好的分离。所得珠铁中碳、硫的质量分数分别为3.53%和0.17%,珠铁的内部组织结构主要由珠光体和渗碳体组成。渣中以硅酸钙（CaSiO3）和硅酸二钙（Ca2SiO4）为主,含有少量的钙镁橄榄石（CaMgSiO4）和玻璃体。计算得知：炉料带入的硫中24.61%进入渣、61.91%进入铁、13.48%进入空气。
The reduction experiment was carried out, using carbon-bearing pellets which were mainly made of iron concentrate, pulverized coal and limestone, at 1 573 K, 1 623 K, 1 673 K with different heating time. The distribution of sulfur was also calculated. The results show that： at 1673K, 12min, iron nuggets and slag can separate well. The carbon and sulfur content of nuggets is 3.53 % and 0.17 %, the internal organizational structure of nuggets con- sists mainly of pearlite and cementite. The slag mainly contains calcium silicate （CaSiOa） and dicalcium silicate （Ca2 SiO4 ）, and the others are monticellite （CaMgSi04） and vitreous. About 24.61% of sulfur is entering the slag, and 61.91% into the iron, 13.48%get into the air.
参考文献
| [1] | 魏国,赵庆杰,董文献,王治卿.直接还原铁生产概况及发展[J].中国冶金,2004(09):16-20. |
| [2] | 赵沛,郭培民.煤基低温冶金技术的研究[J].钢铁,2004(09):1-6,13. |
| [3] | 唐恩,周强,秦涔,阮建波.转底炉处理含铁原料的直接还原技术[J].炼铁,2008(06):57-60. |
| [4] | 黄洁.谈转底炉的发展[J].中国冶金,2007(04):23-25,58. |
| [5] | Larry Lehtinen;Jeff Hansen .Iron dynamics process: a new way to make iron[J].AISE Steel Technology,1999(12):37-39. |
| [6] | W-K. LU .The Search for an Economical and Environmentally Friendly Ironmaking Process[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2001(5):757-762. |
| [7] | B. Anameric;S.K. Kawatra .Laboratory study related to the production and properties of pig iron nuggets[J].Minerals & Metallurgical Processing,2006(1):52-56. |
| [8] | Anameric B;Rundman K B;Kawatra S K .Carburization Effects on the Pig Iron Nugget Making[J].Minerals &Met allurgical Processing,2006,23(03):139. |
| [9] | Kazuhiro NAGATA;Rie KOJIMA;Taichi MURAKAMI .Mechanisms of Pig-iron Making from Magnetite Ore Pellets Containing Coal at Low Temperature[J].ISIJ International,2001(11):1316-1323. |
| [10] | Basak ANAMERIC;S. Komar KAWATRA .The Microstructure of the Pig Iron Nuggets[J].ISIJ International,2007(1):53-61. |
| [11] | Ichiro SEKI;Kazuhiro NAGATA .Reduction kinetics of hematite powder mechanically milled with graphite[J].ISIJ International,2006(1):1-7. |
| [12] | Iguchi Y;Endo S .Reactions,Coalescence of Reduced Iron Particles,and Liberation of Carbon Particles in Carbon Corn posite Iron Ore Pellets[J].ISIJ International,2004,44(12):1999. |
| [13] | Ko-ichiro OHNO;Takayuki MAEDA;Koki NISHIOKA .Effect of Carbon Structure Crystallinity on Initial Stage of Iron Carburization[J].ISIJ International,2010(1):53-58. |
| [14] | Iguchi Y;Endo S .Carburized Carbon Content of Reduced I- ron and Direct Carburization in Carbon Composite Iron()re Pellets Heated at Elevated Temperature[J].ISIJ International,2004,44(12):1991. |
| [15] | 段东平,万天骥,郭占成.硫在含碳球团内的转化行为[J].钢铁研究学报,2005(05):16-21. |
| [16] | 黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,2004 |
| [17] | 蔡九菊,吴复忠,李军旗,张金柱.高炉-转炉流程生产过程的硫素流分析[J].钢铁,2008(07):91-95. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%