以Inconel718气雾化预合金粉末为原料,采用金属注射成形(MIM)工艺制备Inconel718合金材料.研究Inconel718合金烧结、热等静压(HIP)、热处理对合金显微组织、密度和力学性能的影响.结果表明:经1275 ℃烧结后,烧结体的相对密度达到98%.烧结体经HIP处理后,达到全致密.经烧结+HIP+热处理后,组织弥散析出了大量的γ″相和γ′相,其室温抗拉强度为1250 MPa,延伸率为21.7%;650 ℃抗拉强度为1177 MPa,延伸率为16.6%,其达到或超过了同牌号锻造合金的性能.
Effects of sintering temperature, hot isostatic pressing(HIP)and heat-treatment on the microstructure, density and mechanical properties of Inconel718 alloy prepared by metal injection molding were investigated. The results show that the sintered alloy with a relative density of 98% can be achieved at 1275 °C. After HIP process, full density was achieved. After heat-treatment, a large amount of γ″ and γ′ phase were precipitated which increases the tensile strength and decreases the elongation of the alloy. The tensile strength and elongation were 1250 MPa and 21.7%, respectively, at room temperature, and 1177 MPa and 16.6% at 650 °C respectively, which are comparable with or superior to those of the wrought alloy.
参考文献
| [1] | Johnson J L;Tan L K;Suri P.Advances in Powder Metallurgy& Particulate Materials 2004[M].Princeton:Metal Powder Industries Federation,2004:4-89-101. |
| [2] | 李益民,黄伯云,曲选辉.金属注射成形技术进展[J].稀有金属材料与工程,1996(01):1-4. |
| [3] | 李益民,黄伯云,钟伟.工艺参数对金属注射成形坯缺陷的影响[J].稀有金属材料与工程,1999(02):117-120. |
| [4] | 李益民,曲选辉,黄柏云.金属注射成形喂料的流动行为及粘度参数的测定[J].稀有金属材料与工程,1997(01):41-43. |
| [5] | 李益民,K.A.Khalil,黄伯云.金属注射成形17-4PH不锈钢脱脂保形性研究[J].稀有金属材料与工程,2005(01):22-27. |
| [6] | Davies P;Dunstan G;Hoyward A.[A].Shrewsbury:European Powder Metallurgy Association,2004:6. |
| [7] | Bose A;Valencia J;Spirko J et al.[J].Advances in Powder Metallurgy and Particulate Materials,1997,18(05):99. |
| [8] | Bose A;Valencia J;Spirko J et al.[J].Advances in Powder Metallurgy and Particulate Materials,1997,18(05):99. |
| [9] | Rao G;Kumar M;Srinivas M.[J].Materials Science and Engineering A,2003:114. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%