利用热膨胀法,通过Gleeble1500热模拟机测定了P92钢焊接连续冷却转变过程中的膨胀曲线.采用共聚焦显微镜,扫描电镜对不同冷却速度下的试样进行显微组织观察及分析;利用显微硬度计测量了不同冷速下的显微硬度.通过对P92钢连续冷却特性分析和比较得出P92钢的焊接连续冷却转变曲线(SH-CCT曲线).结果表明,P92钢的焊接CCT曲线分为两个区域,在高温区的类珠光体转变区,在低温区的马氏体转变区.P92钢在0.01 ~0.1℃/s的冷速范围内获得类珠光体+马氏体+残留奥氏体的混合组织;当冷却速度大于等于0.5℃/s时,获得马氏体与残留奥氏体的混合组织.

参考文献

[1] 戴长清,田富强,轩福贞.超超临界锅炉管道用T92/P92钢蠕变性能[J].压力容器,2010(03):40-45.
[2] 王学,潘乾刚,陈方玉,陶永顺,彭芳芳.P92钢高温蠕变损伤分析[J].材料热处理学报,2010(02):65-69.
[3] 乔亚霞,武英利,郭军.P92钢焊接接头持久强度及微观组织分析[J].焊接学报,2011(01):109-112.
[4] A. A. Saad;T. H. Hyde;W. Sun;C. J. Hyde;D. W. J. Tanner.Characterization of viscoplasticity behaviour of P91 and P92 power plant steels[J].International Journal of Pressure Vessels and Piping,2013:246-252.
[5] Lei Zhao;Hongyang Jing;Lianyong Xu;Junchao An;Guangchun Xiao .Numerical investigation of factors affecting creep damage accumulation in ASME P92 steel welded joint[J].Materials & design,2012(Feb.):566-575.
[6] WANG Xue;PAN Qian-gang;REN Yao-yao et al.Microstructure and type Ⅳ cracking behavior of HAZ in P92 steel weldment[J].Materials Science and Engineering A,2012,552:493-501.
[7] Kannan R;Sankar V;Sandhya R et al.Comparative evaluation of the low cycle fatigue behaviours of P91 and P92 steels[J].Procedia Engineering,2013,55:149-153.
[8] 张红军;周荣灿;唐丽英.P92钢650℃时效的组织性能研究[J].中国电机工程学报,2009(z1):174-177.
[9] 刘睿,邹勇,张忠文,杜宝帅.超超临界机组用P92钢高温服役8000 h后显微组织与韧性[J].材料热处理学报,2014(09):116-120.
[10] 刘福广,李太江,梁军,姚兵印,王彩侠.高温时效对P92钢焊接接头显微组织和力学性能的影响[J].中国电机工程学报,2011(14):121-126.
[11] Yrostková V';Homolová V;Pecha J et al.Phase evolution in P92 and E911 weld metals during aging[J].Materials Science and Engineering A,2008,480(1/2):289-298.
[12] Guo, X.;Gong, J.;Jiang, Y.;Rong, D..The influence of long-term aging on microstructures and static mechanical properties of P92 steel at room temperature[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2013:199-205.
[13] 张忠文,李新梅,刘非凡,吴崇志,吴军.焊接方法对T92钢焊接接头韧性的影响[J].热加工工艺,2007(03):36-38.
[14] Nai-qiang Zhang;Hong Xu;Bao-rang Li;Yang Bai;Dong-yu Liu .Influence of the dissolved oxygen content on corrosion of the ferritic-martensitic steel P92 in supercritical water[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(Mar.):123-128.
[15] Kaiju Yin;Shaoyu Qiu;Rui Tang .Corrosion behavior of ferritic/martensitic steel P92 in supercritical water[J].The Journal of Supercritical Fluids,2009(3):235-239.
[16] 胡淑娥.600MPa级耐火钢焊接热模拟研究[J].热加工工艺,2005(02):57-58,64.
[17] 刘宗昌,李文学,邵淑艳.工模具钢退火用C曲线的测定及其应用[J].金属热处理,2001(07):36-37.
[18] 王艳杰,何长红,彭云,田志凌,许良红.控轧控冷与热轧耐候钢焊接CCT曲线测定及热影响区的组织特征[J].焊接,2007(11):45-48,60.
[19] 刘宗昌.材料组织转变原理[M].北京:冶金工业出版社,2006
[20] 周世锋,王昱成,李向阳,周宝金,李滨,李伟东.ZGOCr13Ni5Mo马氏体不锈钢模拟焊接HAZ组织与性能[J].焊接学报,2004(04):63-66.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%