采用动电位扫描技术测量304不锈钢在3．5％NaCl溶液中不同电位扫描速率下的极化曲线，用电子散斑干涉技术（ESPI）结合动电位扫描测量304不锈钢在不同浓度、温度和pH值的NaCl溶液中的点蚀电位。结果表明，电位扫描速率为0．3—6mV／s时，其对304不锈钢在NaCl溶液中的自腐蚀电位和点蚀电位以及滞后环的大小的影响较小。电子散斑干涉技术测量的点蚀电位表明304不锈钢的点蚀敏感性随着溶液浓度和温度的增加而增大，随着溶液pH值的增加而减小。
The polarization curves of 304 stainless steel in 3.5% NaCl solution at different potential scanning speed was measured by dynamic potential scanning method, and its pitting potential in NaCl solution with different concentration, temperature and pH value was investigated by electronic speckle pattern interferometer (ESPI) and dynamic potential scan technique. The result indicated that the influence of potential scanning speed on corrosion potential, pitting potential and the size of the hysteresis loop of 304 stainless steel was little when it was 0.3-6 mV/s. The pitting corrosion sensitivity of 304 stainless steel increased with solution concentration and temperature rising and reduced with pH value rising.
参考文献
| [1] | 曹占锋,乔利杰,褚武扬,张继枚,齐新.321不锈钢点蚀电位影响因素的研究[J].中国腐蚀与防护学报,2006(01):22-25,30. |
| [2] | 郝献超,苏鹏,肖葵,董超芳,李晓刚.不同NaCl浓度对耐候钢腐蚀产物的影响[J].腐蚀与防护,2009(05):297-299. |
| [3] | 秦瑞杰,路敏,郭未宽,牛林.酸性氯化物溶液中不锈钢点蚀的局部电化学扫描研究[J].腐蚀科学与防护技术,2009(03):230-232. |
| [4] | A. Poursaee .Determining the appropriate scan rate to perform cyclic polarization test on the steel bars in concrete[J].Electrochimica Acta,2010(3):1200-1206. |
| [5] | 王梅丰,杜楠,李晓刚,赵晴,刘刚.利用电子散斑干涉技术研究45碳钢在NaHCO3-Nacl体系中的早期点蚀行为[J].中国腐蚀与防护学报,2009(03):210-214. |
| [6] | 王梅丰 .利用激光电子散斑研究金属点蚀早期腐蚀行为及机理[D].北京科技大学,2008. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%