采用软模板法和自模板法分别制备了Cu2O空心球,探索了不同制备方法下反应条件对Cu2O空心球形貌及性能的影响,研究了以其作为防污剂制备的涂层防海洋污损生物的防污性能.通过X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和抑菌测试等手段表征和探讨了Cu2O空心球的抑菌性能.结果表明:用软模板法得到表面光滑、结晶度高的Cu2O空心球;用自模板法制备得到由纳米粒子组成的开口空心微球.在抑菌试验中,2种空心球浊液浓度为50 μg/mL时,抑菌作用均可以达到95％以上,抑菌效果好.将2种Cu2O空心球作为防污剂与含氟嵌段共聚树脂SBF改性树脂混合,得到2种杂化防污涂层.通过SEM进行表征,在抗藻类附着试验中,表面基本没有藻类附着,具有良好的防污性能.在浸泡过程中,2种杂化涂层的表面形成了不同的特殊纳米结构表面形貌,这应是少量Cu2O空心球即可使杂化涂层具有好的防污效果的原因.
Two kinds of Cu2O hollow microspheres were prepared by soft-templating method and self-templating method.The effects of different reaction conditions on the morphology and performance of Cu2O hollow spheres were studied.XRD,SEM and TEM were utilized to characterize the antibacterial property of Cu2O hollow spheres.The results showed that the hollow microsphere with perfect ball-shape could be successfully prepared by soft-templating method,at mean time,the hollow Cu2O microsphere with open-mouth was prepared through self-templating method.The antibacterial experiment results showed when the turbid liquid concentration of two hollow microspheres reached 50 μg/mL,the antibacterial effect could reach more than 95％,indicating that the two hollow microspheres had good antibacterial properties.Using SBF as the film-forming agent,two kinds of synthesized Cu2O hollow microspheres as anti-fouling agent respectively,two kinds of hybrid coatings were prepared.The two kinds of SBF-Cu2O hollow microspheres film showed anti-algae performance.SEM revealed that the micro-nanometer structure was formed on the surface of the two hybrid coatings and no algae attached thereto as they were soaked in algae solution,indicating that the films with less Cu2O hollow microspheres had better antifouling performance.
参考文献
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%