通过溶胶-凝胶法，以载玻片为基底制得非晶型纳米TiO2薄膜，用SEM、XPS、XRD和接触角测量仪研究了薄膜的微观形貌、表面元素、晶型结构及薄膜的疏水性，用Wenzel、Cassie理论对纳米TiO2薄膜的润湿性进行了理论分析。结果表明，经紫外光照射16h后，薄膜表面由超疏水性变为超亲水性，接触角接近0°。薄膜表面合适的粗糙度和低表面能材料表面修饰的协同作用使其表现出良好的超疏水性。
A non- crystal nanometer titanium oxide film was fabricated on the glass substrate with a method of sol-gel, SEM, XPS, XRD and contact angle meter were employed to characterize its surface morphologies, elements contained, crystal structure and wettability, respectively. The wettability of the film was discussed on the basis of Wenzel's and Cassie's theory. The results show that the film changes from superhydrophobicity to superhydrophilicity with a static contact angle of 0° after being irradiated under ultraviolet light for about 16 hours. The superhydrophobic properties are caused by the cooperation effect of appropriate surface roughness and surface modification of low surface energy material.
参考文献
| [1] | Wagner P, Fiirstner R, Barthlott W, et al. Quantitativeassessment to the structural basis of water repellency innatural and technical surfaces [J]. J Exp Bot, 2003, 54(385):1295-1303. |
| [2] | Barthlott W, Neinhuis C. Purity of the sacred lotus, or escapefrom contamination in biological surfaces [J]. Planta,1997,202(1): 1-8. |
| [3] | Feng L,Li S H, Li Y S. Super - hydrophobic surfaces: Fromnatural to artificial [J], Adv Mater, 2002,14(24) : 1857 -1860. |
| [4] | Parker A R,Lawrence C R. Water capture by a desert beetle[J]. Nature, 2001, 414, 33-34. |
| [5] | Gao X F, Yan X,Yao X,et al. The dry - style antifoggingproperties pf mosquito compound eyes and artificial analoguesprepared by soft lithography [J], Adv Mater, 2007, 19(17):2213-2217. |
| [6] | Tsujii K, Yamamoto T. Onoue Y. Super oil-repellent surfaces[J]. Angew Chem Int Ed Engl, 1997, 36(9) : 1011-1012. |
| [7] | FresnaisJ,Chapel J P,Poncin - Epaillard F. Synthesis oftransparent superhydrophobic polyethylene surfaces [J]. Surfaceand Coating Technology , 2006,200(18/19) : 5296-5303. |
| [8] | Woodward I,Schofield W C E,Roucoules V. Super -hydrophobic surfaces produced by plasma fluorination ofpolybutadiene films [J]. Langmuir, 2003,19,3432-3438. |
| [9] | He B, Patankar N A, Lee J. Multiple equilibrium dropletshapes and design criteria for rough hydrophobic surfaces [J].Langmuir, 2003, 19(12) : 4999-5003. |
| [10] | Li S H, Li H J, Wang X B, et al. Super - hydrophobicity oflarge - area honeycomb - like aligned carbon nanotubes [J]. JPhys Chem B, 2002, 106(36): 9274-9276. |
| [11] | Guo C W, Feng L,Zhai J. Large - area fabrication of ananostructure-induced hydrophobic surface from a hydrophilicpolymer [J]. Chem Phys Chem, 2004, 5(5) : 750-753. |
| [12] | Han J T, Lee D H, Ryu C Y. Fabrication ofsuperhydrophobic surface from a supramolecular organosilanewith quadruple hydrogen bonding [J]. J Am Chem Soc,2004,126(15): 4796-4797. |
| [13] | Feng X J, Zhai J,Jiang L. The fabrication and switchablesuperhydrophobicity of T1O2 nanorod films [J]. Angew ChemInt Ed, 2005, 44(32): 5115-5118. |
| [14] | Jiang Z X,Geng L, Huang Y D. Design and fabrication ofhydrophobic copper mesh with striking loading capacity andpressure resistance [J]. J Phys Chem C,2010,114(20):9370-9378. |
| [15] | Morra M, Occhiello E, Garbassi F. Contact angle hysteresisin oxygen plasma treated poly (tetrafluoroethylene) [ J ].Langmuir, 1989, 5(3) : 872-876. |
| [16] | 石金娥,闫吉昌,尚淑霞.二氧化钛纳米粒子和纳米管的合成、表征及对硝基苯的光催化性能降解[J].高等学校化学学报,2007,28(7): 1325-1328. |
| [17] | Hoffmann M R, Martin S T, Choi W Y, et al. Environmentalapplications of semconductor photocatalysis [J]. Chem Rev,1995, 95(1): 69-96. |
| [18] | Gratzel M. Photoelectrochemical cells [ J]. Nature, 2001,414: 338-244. |
| [19] | 童玉清,田明,徐瑞芬,等.新型的高杀菌纳米二氧化钛/聚丙烯复合材料的结构和物理特性研究[J].复合材料学报,2003, 20(5); 88-94. |
| [20] | TadanagaK, Morinaga J, Minami T. Formation ofsuperhydrophilic pattern of flowerlike alumina thin film by thesol-gel method [ J ]. Journal of Sol-Gel Science andTechnology, 2000,19(1/2/3): 211-214. |
| [21] | Wenzel R N. Resistance of solid surfaces to wetting by water[J]. Ind Eng Chem, 1936, 28,988-994. |
| [22] | Cassie A B D, Baxter S. Wettability of porous surfaces [J].Trans Faraday Soc, 1944, 40: 546-551. |
| [23] | Wang R, Hashimoto K,Fujishima A, et al. Photogenerationof highly amphiphilic TiO2 surfaces [J]. Adv Mater, 1998,10(2): 135-138. |
| [24] | Xu W G,Liu H Q, Xi J M,et al. Fabrication ofsuperhydrophobic surfaces with hierarchical structure througha solution - immersion process on copper and galvanized ironsubstrates [J]. Langmuir, 2008,24(19) : 10895-10900. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%