采用阳极氧化法在钛金属表面制备TiO_2薄膜,将表面改性的钛金属在过饱和钙化溶液中浸泡,在其表面沉积羟基磷灰石,研究了退火处理温度对TiO_2薄膜晶型转变的影响以及TiO_2的晶型结构对羟基磷灰石的诱导沉积作用.研究表明,300℃退火处理,TiO_2薄膜为板钛矿相,500℃退火处理转变为锐钛矿相,高于500℃退火处理,锐钛矿相开始向金红石相转变.其中锐钛矿相的TiO_2对羟基磷灰石的沉积具有最好诱导作用,沉积物分布均匀,板钛矿相对羟基磷灰石的诱导作用最差,所形成的沉积层是由片状的羟基磷灰石围成的多孔结构.
TiO_2 film was prepared on surface of pure titanium by anodie oxidation method. A layer of hydroxyapatite was coated on the oxidized surface of the titanium sample, which was immersed into a supersaturated calcified solution. The effects of annealing temperature on the transitions of TiO_2 crystalline strcture and the inducing effects of TiO_2 crystalline streture on the deposition of hydroxyapatite were investigated. It is shown that the crystalline of TiO_2 film annealed at 300 ℃ is brookite, and transforms into anatasc when annealed at 500 ℃. The TiO_2 film turns into rutile with the annealing temperature over 500 ℃. The best inducing effect of anatase TiO_2 film on the deposition of hydroxyapatite is be observed and the hydroxyapatite coating is well-distributed. The brookite TiO_2 film results in the worst inducing effect for the deposition of hydroxyapatite. The formed coating is uniform porous which consists of flake hydroxyapatite.
参考文献
| [1] | Block M S;Finger I M;Fontenot M G et al.Loaded hydroxyapatite-coated and grit-blasted titanium implants in dogs[J].International Journal of Oral & Maxillofacial Implants,1989,4:219-2225. |
| [2] | Liu XY;Chu PK;Ding CX .Surface modification of titanium, titanium alloys, and related materials for biomedical applications[J].Materials Science & Engineering, R. Reports: A Review Journal,2004(3/4):49-121. |
| [3] | Kokubo T;Kim HM;Kawashita M .Novel bioactive materials with different mechanical properties.[J].Biomaterials,2003(13):2161-2175. |
| [4] | Aladjem A .Anedic oxidation of titanium and its alloys[J].Journal of Materials Science,1973,8(05):688-6704. |
| [5] | Lausmaa J;Kasemo B;Mattsson H et al.Multi-technique surface characterization of oxide films on electropolished and anodically oxidized titanium[J].Applied Surface Science,1990,45(03):189-1200. |
| [6] | Serruys Y;Sakout T;Gorse D .Anodic oxidation of titanium in 1 M H_2SO_4 studied by rutherford backscattering[J].Surface Science,1993,282(03):279-2287. |
| [7] | Li P;Kangasniemi I;Groot K D et al.Bonelike hydroxyapatite induction by a Gel-derived titania on a titanium substrate[J].Journal of the American Ceramic Society,1994,77(05):1307-11312. |
| [8] | Uchida M;Kim H M;Kokubo T et al.Structural dependence of apatite formation on titania gels in a simulated body fluid[J].Journal of Biomedical Materials Research Part A,2003,64:164-170. |
| [9] | Wu J M;Hayakawa S;Tsuru K et al.Porous titania films prepared from interactions of titanium with hydrogen peroxide solution[J].Scripta Materialia,2002,46(01):101-1106. |
| [10] | Oh J S;Lee Y H;Kang B A et al.Biomimetic formation of calcium phosphate on thermally oxidized cp-titanium surfaces[J].Ceramics International,2003,29(07):847-8849. |
| [11] | Chi-Min Lin;Shiow-Kang Yen .Biomimetic growth of apatite on electrolytic TiO_2 coatings in simulated body fluid[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2006(1):54-64. |
| [12] | Lin C M;Yen S K .Characterization and bond strength of electrolytic HA/TiO_2 double layers for orthopaedic applications[J].Journal of Materials Science:Materials in Medicine,2005,16(10):889-8897. |
| [13] | Kim HW;Koh YH;Li LH;Lee S;Kim HE .Hydroxyapatite coating on titanium substrate with titania buffer layer processed by sol-gel method.[J].Biomaterials,2004(13):2533-2538. |
| [14] | D. Velten;V. Biehl;F. Aubertin .Preparation of TiO_2 layers on cp-Ti and Ti6Al4V by thermal and anodic oxidation and by sol-gel coating techniques and their characterization[J].Journal of biomedical materials research, Part B. Applied biomaterials,2002(1):18-28. |
| [15] | 付涛,憨勇,徐可为,何莉萍,米耀荣.溶胶-凝胶法二氧化钛薄膜诱导沉积磷酸钙层[J].硅酸盐学报,2003(04):402-405. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%