目前,有关镀液中F-对镁合金化学镀镍影响的研究还不系统.探讨了AZ91D镁合金化学镀镍液中NH4HF2浓度对化学镀镍初始沉积、镀液缓冲力和镀层的沉积速率、结合力、形貌、耐蚀性的影响.结果表明:F-对镀镍初始沉积有较大影响,若镀液中无NH4 HF2时,AZ91D镁合金化学镀镍将难以进行,如果先在含F-的镀液中施镀适当时间后,再放入无F-镀液中施镀,镀镍能顺利进行;随着镀液中NH4HF2浓度的增加,镀液的缓冲性能越来越好,镀层的结合力先增强后减弱,镀层沉积速率和腐蚀速率先减小后增大,镀层胞状物先变小后变大,镀层致密性先变好后变差;当镀液中加入20 g/L NH4 HF2时,镀层综合性能最好.

参考文献

[1] A.A. Zuleta;E. Correa;M. Sepulveda;L. Guerra;J.G. Castano;F. Echeverria;P. Skeldon;G.E. Thompson .Effect of NH_4HF_2 on deposition of alkaline electroless Ni-P coatings as a chromium-free pre-treatment for magnesium[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(Feb.):194-200.
[2] Ying HG;Yan A;Ma TY;Wu JM;Yu LQ .Effects of NH4F on the deposition rate and buffering capability of electroless Ni-P plating solution[J].Surface & Coatings Technology,2007(2):217-221.
[3] ASTM B480-1988.Standard guide for preparation of magnesium and magnesium alloys for electroplating[S].
[4] 国栋,樊占国,杨中东,赵林,高鹏.镁合金化学镀中预处理氟化镁膜的特征与作用[J].中国有色金属学报,2007(05):789-794.
[5] 安茂忠.电镀理论与技术[M].哈尔滨:哈尔滨工业大学出版社,2004:259.
[6] 姜晓霞;沈伟.化学镀理论及实践[M].北京:国防工业出版社,2000:55.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%