采用NF1201水相封孔剂对金手指进行封孔处理.通过中性盐雾试验、稀硝酸浸泡试验、饱和二氧化硫试验及电路导通测试等研究了NF1201的耐蚀节金性能.结果表明,NF1201封孔剂的耐蚀节金性能和导电性良好.镀0.3 μm薄金的金手指经NF1201处理后,其耐中性盐雾、耐硝酸及耐二氧化硫腐蚀性能优于未经NF1201处理的镀0.88 μm厚金的金手指,电路微阻未显著改变.
参考文献
| [1] | 付明,张宝根.浅议金镀层表面腐蚀机理及抗腐蚀性保护[C].第九届全国转化膜及表面精饰学术年会论文集,2012:99-103. |
| [2] | 张宝根 .正确地选择电接触材料[J].机电元件,1992,12(04):6-12,53. |
| [3] | Ghaziof, S.;Raeissi, K.;Golozar, M.A. .Improving the corrosion performance of Cr-C amorphous coatings on steel substrate by modifying the steel surface preparation[J].Surface & Coatings Technology,2010(7):2174-2183. |
| [4] | KUDRAK E J;ABYS J A;HUMIEC F .The impact of substrate roughness on porosity:a comparison of electro-plated palladium,palladium-nickel & cobalt hard gold[J].Plating & Surface Finishing,1997,84(01):32-37. |
| [5] | REHRIG D L .Effect of deposition method on porosity in Au thin films[J].Plating,1974,61(01):43-47. |
| [6] | NOTTER I M;GABE D R .Porosity ofelectrodeposited coatings:its cause,nature,effect and management[J].Corrosion Reviews,1992,10(3/4):217-280. |
| [7] | 郑关林.镀金层盐雾试验机理及方法探讨[J].电镀与精饰,1999(06):11-14. |
| [8] | 赵晓利,张宝根.金镀层表面腐蚀机理及抗腐蚀性保护[J].电子工艺技术,2005(06):362-364,369. |
| [9] | 李青,张立新.电气电子产品的腐蚀性气体试验方法[J].电子元件与材料,2003(05):51-54. |
| [10] | 苏仁超,许良军.一种低浓度SO2加速腐蚀试验方法[J].机电元件,2004(04):10-12,33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%