N,N,N',N'-四缩水甘油基-2,2-双[4-(4-氨基苯氧基)苯基]丙烷(TGBAPP)作为一种新型四官能团环氧树脂，因其分子中含有2个柔性基团（醚键）和四个环氧基团，与固化剂反应生成交联网状结构，可作为一种耐热基体树脂。以TGBAPP、DADP248耐高温活性增韧剂、甲基四氢苯酐(MTHPA)为原料，制得一种性能优异的环氧胶粘剂，并对其性能进行了测试。结果表明：该环氧胶粘剂具有良好的疏水性、力学性能和耐热性能。室温、190℃、240℃下拉伸剪切强度分别为30.3 MPa、22.8 MPa、4.8 MPa，表面能为38.0 mJ/m2，远小于水的表面能(72 mJ/m2)，吸水率为1.65%。
N,N,N′,N′-tetralycidyl-2,2-bis[4-(4-aminophenoxy)phenyl]propane (TGBAPP) is a novel tetrafunc-tional epoxy resin. Because TGBAPP molecule contains two flexible groups (ether bond) and four epoxy groups, and it can react with curing agent forming cross-linked structure, therefore it can used as a high temperature resistance matrix resin. Using TGBAPP, high temperature resistance reactive toughener (DADP248), and methyl tetrahydrophthalic anhydride (MTHPA) as raw materials, we prepared a novel epoxy adhesive, and its properties were tested. The results show that the epoxy adhesive has excellent hydrophobicity, mechanical properties, and heat resistance. The tensile shear strength of the novel epoxy adhesive at room temperature, 190℃, and 240℃ is 30.3 MPa, 23.8 MPa, and 4.8 MPa respectively. The surface energy is 38.0 mJ/m2, which is much less than the surface energy of water(72 mJ/m2), and the water absorption rate is 1.65%.
参考文献
| [1] | 4,4'-二氨基二苯基醚四缩水甘油胺的合成[J].首都师范大学学报,1997(03):73. |
| [2] | 何双林.多官能团脂环族环氧树脂的合成[C].第十六次全国环氧树脂应用技术学术交流会暨学会西北地区分会第五次学术交流会暨西安粘接技术协会学术交流会论文集,2012:152-156. |
| [3] | 贺福 .高性能复合材料基体-环氧树脂[J].化工新型材料,1984,12(11):10. |
| [4] | 虞鑫海;徐永芬;赵炯心 等.耐高温单组份环氧胶粘剂的研制[J].粘接,2008,29(12):16-19. |
| [5] | 李恩,虞鑫海,徐永芬,刘万章.高强度单组份环氧胶粘剂的制备及其性能研究[J].绝缘材料,2012(01):12-14. |
| [6] | 程珏;陈静;张军营.新型多官能度环氧树脂的合成、结构与性能[A].北京,2007 |
| [7] | 虞鑫海,刘万章,徐永芬,傅菊荪,赵炯心.4,4'-双（4-氨基苯氧基）- 3,3',5,5'-四甲基联苯及其聚酰亚胺的合成与性能研究[J].绝缘材料,2008(04):16-21. |
| [8] | 虞鑫海,高欣,徐永芬,傅菊荪,石安科,赵炯心.4,4'-双（4-氨基苯氧基）二苯硫醚及其聚酰亚胺的合成与性能研究[J].绝缘材料,2008(05):10-14. |
| [9] | 虞鑫海,虞静远,许梅芳,郑秀秀,徐永芬,钱明球,赵炯心.三甲基间苯二胺型聚酰亚胺薄膜的制备与性能研究[J].绝缘材料,2013(03):60-63. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%