研究近α钛合金TA15经等通道转角挤压工艺(ECAP)加工后的维氏显微硬度及其变化规律.结果表明:TA15合金经ECAP挤压后,显微硬度显著提高,且合金试样外层硬度略高于芯部.合金的显微硬度与组织畸变程度、位错密度、晶粒尺寸以及相组成等密切相关.相变点以下挤压,挤压温度越低,硬度越高;相变点以上挤压,由于挤压后水冷过程中在β相内产生针状马氏体α',硬度明显高于相变点以下挤压.模具转角越小,显微硬度越高.随挤压次数增加,硬度先增大后保持基本不变,而挤压路径对硬度的影响与挤压次数、挤压后细化效果密切相关.TA15合金经ECAP后退火,显微硬度明显降低.
参考文献
| [1] | 黄伯云;李成功;石力开.中国材料工程大典[M].北京:化学工业出版社,2006:566. |
| [2] | Ruslan Z. Valiev;Terence G. Langdon .Principles of equal-channel angular pressing as a processing tool for grain refinement[J].Progress in materials science,2006(7):881-981. |
| [3] | Chen Y J;Li Y J;Walmsley J C et al.[J].Materials Science and Engineering,2010,A527(03):789. |
| [4] | Semenova I P;Raab G I et al.[J].Materials Science and Engineering,2004,A387-389:805. |
| [5] | 杨航航,姚泽坤,高峻,郭鸿镇,刘莹莹,王敏.梯度热处理对Ti_3Al/TC11双合金焊接界面组织和显微硬度的影响[J].稀有金属材料与工程,2010(01):22-26. |
| [6] | Yoshinori Iwahashi;Jingtao Wang;Zenji Horita;Minoru Nemoto;Terence G. Langdon .Principle of equal-channel angular pressing for the processing of ultra-fine grained materials[J].Scripta materialia,1996(2):143-146. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%