利用背散射电子衍射(EBSD)及透射电子显微镜(TEM)技术研究TA15合金不同温度退火后晶界取向差变化情况.结果表明,800 ℃退火处理有少量小角晶界转化为大角晶界;退火温度提高到950 ℃,大角晶界分数大幅度增加;小角晶界转化为大角晶界的平均激活能为151.4 kJ/mol,等于α钛的自扩散激活能,说明了小角晶界向大角晶界转变是由钛原子的自扩散控制;TEM观察结果表明,800 ℃退火处理后亚晶界变为具有六方网络的位错网络,950 ℃退火处理则得到大量的等轴晶.
参考文献
| [1] | 曹圣泉,张津徐,吴建生,陈家光.IF钢再结晶晶粒尺寸、显微织构和晶界特征分布的EBSD研究[J].理化检验-物理分册,2004(04):163-167. |
| [2] | 陈善华,吴杰,管登高,邹丛沛,邱绍宇.金属材料晶界工程研究进展[J].金属热处理,2006(03):1-6. |
| [3] | Glavicic MG.;Kobryn PA.;Bieler TR.;Semiatin SL. .An automated method to determine the orientation of the high-temperature beta phase from measured EBSD data for the low-temperature alpha-phase in Ti-6Al-4V[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):258-264. |
| [4] | Stanford N et al.[J].Acta Materialia,2004,52:5215. |
| [5] | Ivasishin OM.;Semiatin SL.;Markovsky PE.;Shevchenko SV.;Ulshin SV. .Grain growth and texture evolution in Ti-6Al-4V during beta annealing under continuous heating conditions[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):88-96. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%