以整体炭毡为预制体,采用化学气相渗透(CVI)和树脂压力浸渍-常压炭化(PIC)相结合的工艺进行了复合致密,制备了整体毡基炭/炭(C/C)复合材料.通过对不同热处理工艺下材料的轴向热膨胀行为测试,结果表明:当热处理温度从1800℃升至2500℃时,材料1000℃的热膨胀系数(CTE)由3.30×10-6/℃降低到3.00×10-6/℃；当热处理次数由1次增至2次时,材料1000℃的热膨胀系数由2.28×10-6/℃降低为2.10× 10-6/℃.同时发现,当孔隙率相差84％时,热膨胀系数降低约24％.通过研究认为,热处理改变了C/C材料的微观结构,增强了材料石墨化的程度,提高了开口气孔率,可以通过合适的热处理工艺,降低材料的热膨胀系数,提高材料的热稳定性.
参考文献
| [1] | Savage G.Carbon-carbon composites[M].Cambridge:Great Briaina the University Press,1993 |
| [2] | Luo Ruiying .Effect of additives on mechanical properties of oxidation-resistant carbon/carbon composite fabricated by rapid CVD method[J].Carbon: An International Journal Sponsored by the American Carbon Society,2000(15):2109-2115. |
| [3] | Siron O.;Tsuda H.;Yamauchi H.;Maeda K.;Kosaka K.;Chollon G. .Microstructural and mechanical properties of filler-added coal-tar pitch-based C/C composites: the damage and fracture process in correlation with AE waveform parameters[J].Carbon: An International Journal Sponsored by the American Carbon Society,2000(9):1369-1389. |
| [4] | 邓景屹,刘文川,杜海峰.C/C复合材料的抗热应力因素[J].材料研究学报,2001(03):372-374. |
| [5] | 周红英,舒武炳,刘建军,程文,邹武,黄寒星.高温热处理与C/C复合材料性能关系研究[J].固体火箭技术,2007(01):68-71,79. |
| [6] | 李晔,黄启忠,王林山.树脂浸渍法对炭/炭复合材料力学性能的影响[J].新型炭材料,2003(02):117-122. |
| [7] | 廖晓玲,李贺军,孙国栋,李克智.3D C/C复合材料的热膨胀性能[J].新型炭材料,2010(01):60-64. |
| [8] | 张青,成来飞,张立同,徐永东.高温处理对3D C/SiC复合材料热膨胀性能的影响[J].复合材料学报,2004(04):124-128. |
| [9] | 黄伯云;熊翔.高性能炭/炭航空制动材料的制备技术[M].长沙:湖南科学技术出版社,2007:6. |
| [10] | 关振铎.无机材料物理性能[M].北京:清华大学出版社,1992:3. |
| [11] | 张雨雷,李贺军,付前刚,李克智,欧阳海波.炭/炭复合材料表面预炭层的制备及其性能研究[J].无机材料学报,2009(01):125-128. |
| [12] | 张伟刚.化学气相沉积--从烃类气体到固体碳[M].北京:科学出版社,2007:8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%