高纯净度钢的生产是21世纪钢铁企业面临的重大课题,对钢中全氧含量和夹杂物含量的控制是生产高纯净IF钢的关键技术。为此笔者提出一种全新的夹杂物控制技术——反应诱发微小异相去除钢液中细小夹杂物的工艺,设计了一种具有该种功能的复合球体,并开展了工业现场试验研究。试验结果表明：反应诱发微小异相去除细小夹杂物工艺是一种成本低、效率高、简便易行的夹杂物控制技术,它可以显著降低IF钢中非金属夹杂物数量。与传统工艺相比,采用该技术对钢液进行处理后,铸坯中氧化物夹杂的数量明显减少,尺寸变小,铸坯的平均w（[TO]）最低可达7×10-6,吨钢成本可降低5～10元。
The production of high purity steel was a major task for the iron and steel enterprises in the 21st century.Decreasing the total oxygen content and the inclusion removal was the key technique to produce the high purity IF steel.A novel fine inclusion removal technology due to the dispersed in-situ phase induced by the composite ball explosive reaction was put forward.A composite ball with the function was designed and prepared using a laboratory model batch type balling disc（at 12 r/min） and the composite ball was fed at the end of RH refining.The results indicate that feeding composite ball in RH furnace is a novel technology and the inclusion in the molten steel can be removed effectively.The treatment time is less than 10 minutes.Compared with conventional inclusion removal technology,the number of the oxide inclusion can be decreased to a lower level and the inclusion size becomes finer.Using this novel technology,the total oxygen in the as-cast slab can approach to 7×10-6 and the steel production cost for per ton can be reduced by 5-10 yuan.
参考文献
| [1] | Takaki S;Kawasaki K;Kimura Y.Mechanical Properties of Ultra Fine Grained Steels[J].Journal of Materials Processing Technology,2001:117,359. |
| [2] | F. G. Caballero;H. K. D. H. Bhadeshia;K. J. A. Mawella .Very strong low temperature bainite[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2002(3):279-284. |
| [3] | Chiaki OUCHI .Development of Steel Plates by Intensive Use of TMCP and Direct Quenching Processes[J].ISIJ International,2001(6):542-553. |
| [4] | Tae-Kyu LEE;H. J. KIM .Effect of Inclusion Size on the Nucleation of Acicular Ferrite in Welds[J].ISIJ International,2000(12):1260-1268. |
| [5] | Hongbin.YIN .Characteristics of Agglomeration of Various Inclusion Particles on Molten Steel Surface[J].ISIJ International,1997(10):946-955. |
| [6] | Tang F P;Bao Y P .Behaviors of Fine Bubbles in the Shroud Nozzle of Ladle and Tundish[J].Journal of University of Science and Technology Beijing,2003,4:23. |
| [7] | 李正邦.钢铁冶金前沿技术[M].北京:冶金工业出版社,1997 |
| [8] | 刘中柱,蔡开科.纯净钢生产技术[J].钢铁,2000(02):64-69. |
| [9] | 朱苗勇;萧泽强.钢的精炼过程数学物理模拟[M].北京:冶金工业出版社,1998 |
| [10] | 王一洲.超低头板坯夹杂物来源分析及控制实践[J].钢铁,2000(11):26-28,38. |
| [11] | WANG Li-tao,ZHANG Qiao-ying,LI Zheng-bang,XUE Zheng-liang.Fundamental of Inclusion Removal from Molten Steel by Rising Bubble[J].钢铁研究学报（英文版）,2004(06):5-9. |
| [12] | Bessho N;Yamasaki H;Fujll T et al.Removal of Inclusion from Molten Steel in Continuous Casting Tundish[J].ISIJ International,1992,32(01):157. |
| [13] | Turkdogan E T .Novel Concept of Cleansing Liquid Steel of Solid Ooxide Inclusions by Culler Injection in Ladle[J].Ironmaking and Steelmaking,2004,31(02):131. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%