采用成熟工艺制备了N型、P型调制掺杂型Si80Ge20基固溶体合金及等化学计量比的均匀掺杂型Si80Ge20基固溶体合金,重点研究了两类固溶体合金的热电性能.结果表明:温度为773 K时,N型系列、P型系列,调制掺杂型固溶体合金较均匀掺杂型的功率因子分别提高了13.6%和49.2%,热电优值ZT分别提高了7.9%和12.9%.
参考文献
[1] | Hicks L D;Drsselhaus M S et al.[J].Physical Review Letters,1993,47(24):16631. |
[2] | Harman T C;Taylor P J;Walsh M P et al.[J].SCIENCE,2002,297(5590):2229. |
[3] | Ananth S Lyengar .Synthesis and Characterization of Micro/Nano Materials for Thermoelectric Applications[D].Ohio:Case Western Reserve University,2010. |
[4] | Venkatasubramanian R;Edward Siivola;Thomas Colpitts et al.[J].NATURE,2001,413(6865):597. |
[5] | Mona Z;Giri J;Gaohua Zhu et at .[J].Nano Letters,2011,11(06):2225. |
[6] | Gong Xiaozhong;Wu Zhenxing;Peng Yucheng.[J].Transactions of Materials and Heat Treatment(材料热处理学报),2012(11):1. |
[7] | Tian Shi.Physical Properties of the Materials[M].Beijing:Beihang University Press,2004:268. |
[8] | Wang Wenhua .The Preparation and Performance of Si80Ge20 Thermoelectric Materials[D].Wuhan:Wuhan University of Technology,2007. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%