目的：提高钛合金的表面硬度和耐磨性能。方法采用激光熔覆工艺,在 TC11钛合金表面制备80% CBN+20% Ti(均为质量分数)熔覆层,分析熔覆层的显微组织、硬度和耐磨性能。结果熔覆层的显微组织沿层深方向分为熔覆区、结合区和过渡区三个区域,区域之间没有明显的裂纹和断层。 CBN膜层的显微硬度最高达到950HV0.2,耐磨性比纯 Ti 熔覆层提高了近14倍。结论在钛合金表面激光熔覆 CBN 抗磨涂层,不仅耐磨损性能良好,而且表面硬度得到了有效提高。
Objective To improve the surface hardness and wear resistance of titanium alloy. Methods An experimental re-search of 80% CBN+20% Ti coating was prepared on TC11 alloy surface using laser cladding technology. The microstructure, hard-ness and wear resistance of the clad coating were analyzed. Results Microstructure analyses showed that the clad coating could be divided into three zones along the depth direction: clad, binding and transition zones, and there were no obvious cracks and faults among the zones. The maximal microhardness of the CBN membrane layer reached 950HV0. 2, and the wear resistance perform-ance of CBN anti-wear coating was nearly 14 times as high as that of pure Ti coating. Conclusion The wear resistance performance of CBN laser clad anti-wear coating on titanium alloy surface was good, and the surface hardness of the titanium alloy was effective-ly improved.
参考文献
| [1] | 刘铭坤,汤海波,方艳丽,等 . 钛合金表面激光熔覆 TiC/Ti-Ti2 Co 涂层耐磨性[J].激光技术,2011,35(4):444-447,452. LIU M K,YANG H B,FANG Y L,et al. Wear Resistance of Laser Clad TiC/Ti-Ti2 Co Coating on Titanium Alloy [J]. Laser Technology,2011,35(4):444-447,452.,2011. |
| [2] | 项坤,王维,杨光,卞宏友,钦兰云,王伟,尚纯,崔宝磊.钛合金单道激光熔覆工艺的研究[J].表面技术,2013(01):91-93,104. |
| [3] | 武万良,黄文荣,杨德庄,等 . Ti-6Al-4V 合金基体上激光熔覆 Ti+TiC 粉末的显微组织[J].激光技术,2003,27(4):307-310. WU W L,HUANG W R,YANG D Z,et al. Microstructure of Laser Clad Ti+TiC Powders on Ti-6Al-4V Alloy Substrate [J]. Laser Technology,2003,27(4):307-310.,2003. |
| [4] | 冯淑容,张述泉,王华明.钛合金激光熔覆硬质颗粒增强金属间化合物复合涂层耐磨性[J].中国激光,2012(02):60-65. |
| [5] | 裴立宅,肖汉宁,祝宝军,谭伟.碳化硼粉末及其复相陶瓷的研究现状与进展[J].稀有金属与硬质合金,2004(04):46-50. |
| [6] | 丁硕,温广武,雷廷权.碳化硼材料研究进展[J].材料科学与工艺,2003(01):101-105. |
| [7] | 杨杭生,聂安民,张健英.立方氮化硼薄膜的最新研究进展[J].物理学报,2009(02):1364-1370. |
| [8] | 马锡英,岳金顺,贺德衍,陈光华.立方氮化硼薄膜的生长特性与粘附性研究[J].物理学报,1998(05):871-875. |
| [9] | 郭桂芳,陈芙蓉,李林贺.激光熔覆技术在钛合金表面改性中的应用[J].表面技术,2006(01):66-69. |
| [10] | 陈浩. 立方氮化硼薄膜的合成和电特性方面的研究[D]. 北京:北京工业大学,2006. CHEN H. Study on Synthesis and Electrical Characteristics of Cubic Boron Nitride Thin Films[D]. Beijing:Beijing U-niversity of Technology,2006.,2006. |
| [11] | GYORGY E,PINO A P D,SERRA P,et al . Depth Profiling Characterization of the Surface Layer Obtained by Pulsed Nd:YAG Laser Irradiation of Titanium in Nitrogen[J].Sur-face and Coatings Technology,2003,173 |
| [12] | KAIEDA Y. Fabrication of Composition-controlled TiNi Shape Memory Wire Using Combustion Synthesis Process and the In-fluence of Ni Content on Phase Transformation Behavior [J]. Science and Technology of Advanced Materials,2003, 4:239-246.,2003. |
| [13] | 李世波,温广武,张宝生.添加TiB2对Ti-B-C复相陶瓷性能的影响[J].材料科学与工艺,2002(01):32-36. |
| [14] | 刘贵仲,钟文华,高原.激光熔覆涂层缺陷的形成及防治[J].表面技术,2012(05):89-92. |
| [15] | 刘世念,苏伟,魏增福,等 . 热喷涂防腐涂层在大气环境中的应用[J].装备环境工程,2013,10(6):72-76. LIU S N,SU W,WEI Z F,et al. Application of Corrosion Resistant Coating of Thermal Spraying in the Atmospheric Environment [J]. Equipment Environmental Engineering, 2013,10(6):72-76.,2013. |
| [16] | 黄祖凤,张冲,唐群华,戴品强,吴波.退火对激光熔覆FeCoCrNiB高熵合金涂层组织结构与硬度的影响[J].表面技术,2013(01):9-13. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%