用高温裂解法在紫铜基底上制备了疏水性碳纳米管膜,通过对此碳纳米管膜进行氟化处理,改善了表面的疏水性.在室温下,实验测得水在这种表面上的接触角在90°～130°之间.以水蒸气为冷凝介质的冷凝传热实验表明,水蒸气在超疏水纳米材料表面上能形成较好的滴状冷凝,冷凝传热膜系数可达40000 W/(m2·K).与纯粹膜状冷凝相比,冷凝传热系数提高3～4倍.分析表明,此碳纳米管膜所产生的附加热阻只占冷凝传热热阻的千分之一,对冷凝传热膜系数的影响可以忽略.
参考文献
| [1] | Jiang L. .Binary cooperative complementary nanoscale interfacial materials[J].Pure and Applied Chemistry,2000(1/2):73-81. |
| [2] | Huanjun Li;Xianbao Wang;Yanlin Song;Yunqi Liu;Qianshu Li;Lei Jiang;Daoben Zhu .Super-"Amphiphobic" Aligned Carbon Nanotube Films[J].Angewandte Chemie International Edition,2001(9):1743-1746. |
| [3] | 翟锦,李欢军,李英顺,李书宏,江雷.碳纳米管阵列超双疏性质的发现[J].物理,2002(08):483-486. |
| [4] | Lin Feng;Zhenglong Yang;Jin Zhai;Yanlin Song;Biqian Liu;Yongmei Ma;Zhenzhong Yang;Lei Jiang;Daoben Zhu .Superhydrophobicity of Nanostructured Carbon Films in a Wide Range of pH Values[J].Angewandte Chemie,2003(35):4217-4220. |
| [5] | 李欢军,朱道本,王贤宝,宋延林,刘云圻,李前树,江雷.超疏水多孔阵列碳纳米管薄膜[J].高等学校化学学报,2001(05):759-761. |
| [6] | Wang X B;Liu Y Q;Zhu D B .Honeycomb-Like Alignments of Carbon Nanotubes Synthesized by Pyrolysis of a Metal Phthalocyanines[J].Appl Phys A:Materials Science and Processing,2000,71(03):347-348. |
| [7] | 李欢军 .阵列碳纳米管膜的浸润性研究[D].北京理工大学,2001. |
| [8] | 李书宏,冯琳,李欢军,翟锦,宋延林,江雷,朱道本.柱状结构阵列碳纳米管膜的超疏水性研究[J].高等学校化学学报,2003(02):340-342. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%