CaO-Al2O3-SiO2-CaF2-MgO was selected as the slag system for desulfurization in LF process.The reaction between steel and slag during desulfurization has been simulated by using Factsage software to study the influence of component on the sulfur distribution ratio.In order to research the influence of CaO content,aluminum powder content and its granularity on desulfurization,laboratory experiments have been carried out in a 200 kg inductive furnace.Results showed that the optimal composition of deep desulfurizer is wCaO=64% and aluminium powder 10% with a granularity of 30 μm.Industrial trials showed that the main composition range of final slag in LF process is wCaO=53.0%-57.0%,wAl2O3=23.4%-25.1%,wSiO2=8.1%-10.0%,and wCaF2=3.2%-4.7%.The sulfur mass percent in steel is lower than 0.0008% with a desulfurization rate above 89%.According to the result of industrial production,this desulfurizer could meet the production requirement for ultra-low sulfur steel,of which sulfur mass percent is under 0.0015%
参考文献
| [1] | Rama B;Dave T.Ladle Slag Treatment for Production of Ultra-Low Carbon Steels[A].[S.l.].Association for Iron and Steel Technology,1993:457. |
| [2] | Mauro P.A New Generation of Ultra High Strength X100/ X120Pipelines:A Breakthrough for Economic Long-Distance Gas Transportation[A].[S.l.].International Society of Offshore and Polar Engineers,2005:31. |
| [3] | Seung Chan Hong;Jae Cheon Ahn;Sang Yong Nam .Mechanical Properties of High-Si Plate Steel Produced by the Quenching and Partitioning Process[J].Metals and Materials International,2007(6):439-445. |
| [4] | YIN Rui-yu;WANG Xin-hua .Discussion on Proper Secondary Refining Methods of Steel Grades for Cold Rolled Sheets (in Chinese)[J].Iron & Steel,2007,42(05):1. |
| [5] | Kimiaki SAKATA .Technology for Production of Austenite Type Clean Stainless Steel[J].ISIJ International,2006(12):1795-1799. |
| [6] | 陈松林,吕延春,庥庆申.硫分配比在LF精炼渣成分优化中的应用[J].炼钢,2009(03):37-41. |
| [7] | Turkdogan E T .Slags and Fluxes for Ferrous Ladle Metallurgy[J].Ironmaking and Steelmaking,1985,12(02):64. |
| [8] | ZHANG Cai-jun;CAI Kai-ke;YUAN Wei-xia et al.Performance Requirements and Productive Feature of Pipeline Steel (in Chinese)[J].Iron & Steel,2006,41(08):31. |
| [9] | YANG Xiao-jiang;XIA Chun-xue;WANG Xiao-ming et al.Practice of Accelerated Desulphurization Process for 150tLF (in Chinese)[J].Steelmaking,2006,22(01):16. |
| [10] | Jonsson P G .Viscosities of Slags and Their Impact on Ladle Refining[J].ISIJ International,1997,37(05):484. |
| [11] | LI Liang .Variety Steel Smelting Practice and Refining Effect Analysis in LF Furnace Process (in Chinese)[J].Research on Iron and Steel,2007,35(06):8. |
| [12] | Sonsinsky D;Sommerville I .The Composition and Temperature Dependence of the Sulfide Capacity of Metallurgical Slags[J].Metallurgical and Materials Transactions,1986,17B:331. |
| [13] | Young R;Duffy J;Hassall G et al.Use of Optical Basicity Concept for Determining Phosphorus and Sulphur Slag-Metal Partitions[J].Ironmaking and Steelmaking,1992,19(03):201. |
| [14] | Nzotta M M;Du S;Seetharaman S .Sulphide Capacities in Some Multi Component Slags Systems[J].ISIJ International,1998,38(11):1170. |
| [15] | 郝宁,王海涛,王新华,李宏,王万军.硫容量和硫分配比的计算及分析[J].北京科技大学学报,2006(01):25-28. |
| [16] | Arthur D. Pelton.Thermodynamic database development-modeling and phase diagram calculations in oxide systems[J].稀有金属（英文版）,2006(05):473-480. |
| [17] | JIN Li-ling;WANG Hai-tao;XU Zhong-bo et al.Control on Low Melting Point Area in a CaO-SiO2-Al2O3-MnO System (in Chinese)[J].Journal of University of Science and Technology Beijing,2007,29(06):574. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%