以气化炉渣为原料,采用挤出成型法,通过力学性能测试、物相组成和显微结构分析,研究了烧成温度和结合剂添加量等工艺条件对制备的轻质隔热墙体材料性能的影响.结果表明:烧成试样的矿物相为钙长石、石英、赤铁矿和莫来石;1000℃烧成时,添加20％(质量分数,下同)粘土可制备出体积密度为1.00 g/cm3、导热系数为0.19W/(m·k)和耐压强度为5.3 MPa的轻质烧结自保温墙体材料;添加30％粘土可制备出体积密度为1.20 g/cm3、导热系数为0.23 W/(m·k)和耐压强度达20.1 MPa的烧结自保温可承重墙体材料;添加40％粘土可制备出体积密度为1.18 g/cm3、导热系数为0.26 W/(m·k)和耐压强度达16.6 MPa的烧结自保温可承重墙体材料.
参考文献
| [1] | Hengwei Liu;Weidou Ni;Zheng Li;Linwei Ma .Strategic thinking on IGCC development in China[J].Energy policy,2008(1):1-11. |
| [2] | 汤云 .利用气化炉渣和煤矸石制备Sialon基复相陶瓷[D].西安建筑科技大学,2011. |
| [3] | R.H. Matjie;Zhongsheng Li;Colin R. Ward;David French .Chemical composition of glass and crystalline phases in coarse coal gasification ash[J].Fuel,2008(6):857-869. |
| [4] | A. Acosta;M. Aineto;I. Iglesias .Physico-chemical characterization of slag waste coming from GICC thermal power plant[J].Materials Letters,2001(4):246-250. |
| [5] | Tao Wu;Mei Gong;Ed Lester;Fuchen Wang;Zhijie Zhou;Zunhong Yu .Characterisation of residual carbon from entrained-bed coal water slurry gasifiers[J].Fuel,2007(7/8):972-982. |
| [6] | 尹洪峰,汤云,任耘,张军战.Texaco气化炉炉渣基本特性与应用研究[J].煤炭转化,2009(04):30-33. |
| [7] | 尹洪峰,汤云,任耘,张军战.气化炉渣合成Ca-α-Sialon-SiC复相陶瓷[J].硅酸盐学报,2011(02):233-238. |
| [8] | 云正,于鹏超,尹洪峰.气化炉渣对铁尾矿烧结墙体材料性能的影响[J].金属矿山,2010(11):183-186. |
| [9] | 彭美勋,蒋建宏,申少华.用高含土建筑垃圾制备免烧墙体材料的实验研究[J].硅酸盐通报,2011(02):482-486. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%