采用热压烧结致密化工艺,在1 550,1 600,1 650℃3个不同的烧结温度下,烧结制备了Si3N4含量从0.25w%到6w%的Al2O3/Si3N4纳米复相陶瓷.对所制备的试样进行了密度、硬度、断裂韧性的测试.实验结果表明,所有试样达到了较高的致密度,且致密度随烧结温度的升高而增加.硬度在Si3N4含量为0.75w%和3w%时达到峰值.韧性在Si3N4含量3 w%达到峰值.材料的性能较纯Al2O3陶瓷有较大幅度提高.
参考文献
| [1] | 姜炜,李凤生,秦润华.纳米复相陶瓷的制备及性能研究进展综述[J].中国陶瓷工业,2004(06):64-69. |
| [2] | 穆柏春.陶瓷材料的强韧化[M].Bering:Metallrugical Industry Press,2002:151-230. |
| [3] | Mitomo M;Tsutsumi M;Tanaka H et al.Grain Growth During Gas-Pressure Sintering of β-Silicon Nitride[J].Journal of the American Ceramic Society,1990,73(08):2441-2445. |
| [4] | 杨南.无机非金属材料测试方法[M].武汉:武汉工业大学出版社,1990:355-358. |
| [5] | Zhan Guo Dong;Joshua Kuntz;Julin Wang et al.AluminaBased Nanocomposites Consolidated by SPS[J].Scripta Materialia,2002,47(05):737-741. |
| [6] | Burden S;Hong J .Comparison of Hot-Isostatically Pressed and Uniaxially Hot-pressed Al2O3-TiC Cutting Tools[J].American Ceramic Society Bulletin,1988,67(06):1003-1009. |
| [7] | 高濂,王宏志,洪金生,宫本大树,DIAZ DE LA TORRE Sebastian.SiC-ZrO2（3Y）-Al2O3纳米复相陶瓷的力学性能和显微结构[J].无机材料学报,1999(05):795-800. |
| [8] | 刘继富.颗粒弥散陶瓷复相材料的设计[J].航空材料学报,1998(04):9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%