为了提高连铸结晶器的使用寿命和生产效率,利用高速火焰喷涂(HVAF)技术在铜基体上制备了镍基涂层,探讨了喷涂粉末中不同比例的Al2O3对镍基涂层抗热疲劳性能的影响及其机理.结果表明:添加50%Al2O3的镍基涂层,抗热疲劳性能得到了明显的提高;Al2O3颗粒的添加,有效地增加了涂层的压应力,提高了涂层与铜基体之间的结合强度,从而显著地提高了涂层的抗热疲劳性能.
参考文献
| [1] | Alejandro S .Tribological behavior of coatings for continuous casting of steel[J].Surface and Coatings Technology,2003,146-147:55-64. |
| [2] | 久保田 昭,高田 正人,掘 胜广,梅山 佑登,山本 圭祐,大迫 清一.采用Ni-Cr合金热喷涂延长连铸结晶器寿命[J].连铸,2001(04):13-14,46. |
| [3] | Legoux J G;Arsonault B;Moreau C.Evaluation of four hish velocity thermal spray gun using WC-10Co-4Cr cermates[A].Montreal,Canada:ASM International,2000:479-486. |
| [4] | Berget J;Rogne T.A summary of recent developments of HVOF sprayed ceramic-metallic coatings for corrosion and wear resistance[A].Ohio,USA:ASM International Materials Park,2001 |
| [5] | Miller R A;Lowell C E .Failure mechanisms of thermal barrier coatings exposed to elevated temperature[J].Thin Solid Films,1982,95(03):265-273. |
| [6] | 伍超群;邓畅光;邓春明.Al2O3对镍基涂层显微结构影响的研究[J].电子显微学报,2008(增刊):97. |
| [7] | 伍超群,周克崧,刘敏,邓畅光,邓春明,李扬.铜基体上超音速火焰喷涂镍基涂层残余应力分析[J].热加工工艺,2006(19):35-38. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%