由于碱激发硅灰粉煤厌复配地质聚合物的韧性较差,本文利用聚丙烯酸树脂TC-200对其进行增韧及表征.结果表明,TC-200最佳掺量为1 wt%时,试样的抗压抗折强度同时增大,压折比减小,韧性显著提高.结合XRD、SEM分析和Griffith理论证实了TC-200可改变粉煤灰基地质聚合物内部的裂缝表面能,从而达到增韧的效果.
参考文献
[1] | Fernando P T;Joao C G;Said J.Alkali-activated binders:a review partl.Historical background,terminology,reaction mechanisms and hydration products[J].Construction and Building Materials,2008(22):1305-1314. |
[2] | 张耀君 .一种粉煤灰基无机聚合物复合胶凝材料及其制备方法[P].CN 101823847 A |
[3] | Shuzheng Zhang;Kecheng Gong;Jianwen Lu .Novel modification method for inorganic geopolymer by using water soluble organic polymers[J].Materials Letters,2004(7/8):1292-1296. |
[4] | Zhang, Y.J.;Wang, Y.C.;Xu, D.L.;Li, S. .Mechanical performance and hydration mechanism of geopolymer composite reinforced by resin[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(27/28):6574-6580. |
[5] | Zhang, Y.J.;Li, S.;Xu, D.L.;Wang, B.Q.;Xu, G.M.;Yang, D.F.;Wang, N.;Liu, H.C.;Wang, Y.C. .A novel method for preparation of organic resins reinforced geopolymer composites[J].Journal of Materials Science,2010(5):1189-1192. |
[6] | JC/T 984-2005.聚合物水泥防水砂浆[S]. |
[7] | 王茹,王培铭.苯丙乳液水泥砂浆横向变形与压折比及其关系[J].建筑材料学报,2008(04):464-468. |
[8] | 张秀芳,徐世烺.不同软化曲线形状对裂缝扩展阻力GR曲线的影响[J].工程力学,2009(02):5-9. |
[9] | 李朝阳,邱大健,谢国先,肖祥定,倪晓雪.纳米SiO2增韧改性环氧树脂的研究[J].材料保护,2008(04):21-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%