籽晶是影响DKDP晶体生长和光学性能的一个重要因素.通过传统降温法,分别利用Z片和[101]晶片作为籽晶,从氘化程度为85%的溶液中生长DKDP晶体并对加工样品进行了相关测试.研究了不同籽晶对DKDP晶体的生长和光学性能的影响.实验表明,[101]晶片籽晶所得DKDP晶体能有效缩短生长周期,晶体损伤阈值提高明显,但光学均匀性和透过性能有所下降.
Seed is the dominating factor which greatly influences the growth and the optical properties of DKDP single crystal. In this paper, DKDP crystals were grown from 85%-deuterated solution by traditional growth method of Z-plate seed and [101]-plate seed respectively. Then some of those crystals were chosen to measure their optical properties. It was found that the laser damage threshold of DKDP crystal grown from [101] plate seed was obviously improved, and could shorten the growth period effectively; while lead to the deterioration in the transmission spectra.
参考文献
| [1] | 张克从;王希民.非线性光学晶体材料科学[M].北京:科学出版社,1996:107-115. |
| [2] | During A;Lamaignère L;Bouchut P et al.[J].Proceedings of SPIE,2004,5647:177-186. |
| [3] | Runkel M;Neeb K;Staggs M et al.[J].Proceedings of SPIE,2001,4679:368-383. |
| [4] | Demange P;Carr C W;Negres R A et al.[J].Optics Letters,2005,30:221-223. |
| [5] | Adams J J;Weiland T L;Stanley J R et al.[J].Proceedings of Spie,2005,5647:265-278. |
| [6] | Negres R A;Kucheyev S O;DeMange P et al.[J].Proceedings of Spie,2005,5647:306-312. |
| [7] | DeMange P;Negres R A;Carr C W et al.[J].Proceedings of Spie,2005,5647:343-354. |
| [8] | Carr C W;Feit M D;Muyco J J et al.[J].Proceedings of Spie,2005,5647:532-539. |
| [9] | Carr C W;Feit M D;Rubenchik A M et al.[J].Proceedings of Spie,2005,5647:494-500. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%