用苯肼对双氰胺进行改性,合成得到一种新型改性双氰胺固化剂LB-A,探讨了LB-A对环氧树脂的固化行为及反应机理.红外光谱和X射线衍射分析表明,苯肼时双氰胺进行改性后,破坏了双氰胺的规整结构和强结晶性,从而较好地解决了双氰胺与环氧树脂混溶性不佳的问题,并且分子中引入了更多的活泼基团,提高了其与环氧树脂的反应活性.差热分析研究结果表明,相对于双氰胺固化E-44环氧树脂的固化条件(160～180℃/20～60min),LB-A固化环氧树脂的固化温度显著降低,其在110℃/40min或90℃/Sh就可以使E-44完全固化,且固化物具有很好的力学性能.
参考文献
| [1] | 蒋英,阙正波,张竞,周鹏来,黄培.固化剂对聚酰亚胺挠性覆铜板剥离强度的影响[J].高分子材料科学与工程,2010(01):54-57. |
| [2] | Kishi H;Naitou T;Matsuda S;Murakami A;Muraji Y;Nakagawa Y .Mechanical properties and inhomogeneous nanostructures of dicyandiamide-cured epoxy resins[J].Journal of Polymer Science, Part B. Polymer Physics,2007(12):1425-1434. |
| [3] | Zhang XH;Liu F;Chen S;Qi GR .Novel flame retardant thermosets from nitrogen-containing and phosphorus-containing epoxy resins cured with dicyandiamide[J].Journal of Applied Polymer Science,2007(4):2391-2397. |
| [4] | Olivier L;Thierry M;Hugues D .A practical guide to arylbiguanides-synthesis and structural characterization[J].Canadian Journal of Chemistry,2005,83(6-7):615. |
| [5] | 石可瑜,侯信,何尚锦,宋旭,杜宗杰,张保龙.含聚醚间隔链的扩链脲改性环氧树脂/双氰双胺固化体系性能研究[J].高分子学报,2002(05):582-586. |
| [6] | K. Raetzke;M.Q. Shaikh;F. Faupel .Shelf stability of reactive adhesive formulations: A case study for dicyandiamide-cured epoxy systems[J].International Journal of Adhesion & Adhesives,2010(2):105-110. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%