采用电化学测试和慢应变速率实验(SSRT)研究了国产X70管线钢在近中性pH和高pH溶液中的应力腐蚀破裂(SCC)行为.结果表明,X70钢在高pH溶液和近中性pH溶液中的阳极极化曲线表现出明显的差异:在高pH溶液中有明显的活化-钝化转变而在近中性pH溶液中则无;在近中性pH溶液中,X70管线钢的开裂模式是穿晶型的,具有准解理特征,并且随着外加阴极电位的降低,SCC敏感性增加,氢致破裂占主导;随温度的下降以及溶液中CO2含量的增加,溶液pH值降低,SCC敏感性增加.在高pH溶液中,在阴极极化时,X70钢表现出与在近中性pH溶液中类似的破裂行为和特征,即SCC敏感性随电位降低而增大,裂纹数目少而大,裂纹易扩展;但在阳极极化时,裂纹数目多而小,易萌生但难扩展.在2种溶液中阳极极化时,均存在SCC敏感电位区.

参考文献

[1] Sridhar N;Dunn D S;Anderko A.Prediction of conditions leading to stress corrosion cracking of gas transmission lines[A].American Society for Testing and Materials (ASTM), West Conshohocken, PA, USA,2000:241.
[2] National Energy Board (NEB .Public Inquiry Concerning Stress Corrosion Cracking on Canadian Oil and Gas Pipelines[R].NEB Report MH-2-95, Calgary, AB,Canada,1996.
[3] King F;Boven G V;Jack T.Predicting the growth of low- and high pH SCC on gas transmission pipelines based on operating conditions[A].NACE International,Houston,2003:127.
[4] 郭浩,蔡殉,杨武.影响管线钢应力腐蚀破裂的力学和材料因素[J].机械工程材料,2002(04):1-5,10.
[5] 刘杏,杨武.天然气长输管线应力腐蚀破裂的敏感环境条件[J].机械工程材料,2002(01):5-12,40.
[6] Rebak R B;Xia Z;Safruddin R et al.Effect of solution composition and electrochemical potential on stress corrosion cracking of X-52 pipeline steel[J].Corrosion,1996,52(05):396.
[7] Kushida T;Nose K;Asahi H .Effects of metallurgical factors and test conditions on near neutral pH SCC of pipeline steels[R].CORROSION/2001, NACE International, Houston, TX, 2001, Paper No. 01213
[8] W. Chen;F. King;E. Vokes .Characteristics of Near-Neutral-pH Stress Corrosion Cracks in an X-65 Pipeline[J].Corrosion: The Journal of Science and Engineering,2002(3):267-275.
[9] Beavers J A;Durr C L;Delanty B S.High-pH SCC: Temperature and Potential Dependence for Cracking in Field Environments[A].,1998
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%