目的了解Au/Ni/Cu多层金属薄膜在热带海洋气候下的失效机制,为研究电子元器件表面腐蚀失效的早期预警提供参考。方法采用磁控溅射法在p型单晶Si (100)基片上沉积Au/Ni/Cu薄膜,在热带海洋气候环境下进行时效实验,采用原子力显微镜及俄歇电子能谱对薄膜失效表面与界面结构微观变化进行研究。结果时效实验初期,Au/Ni/Cu薄膜表面发生了Au原子聚集,形成了不再连续的岛状结构,岛与岛之间产生了表面微裂纹。随着时效时间的延长,表面形成腐蚀洞,腐蚀洞附近有Ni和Cu扩散至Au层表面。时效时间进一步延长后,腐蚀洞的数量增加,面积增大,此时样品处于腐蚀末期;与此同时,在未产生腐蚀洞的区域,Au/Ni/Cu薄膜界面未出现明显粗化。结论Au/Ni/Cu薄膜在热带海洋气候中的失效主要是通过表面产生的腐蚀洞进行的。

ABSTRACT:Objective To investigate the failure mechanism of Au/Ni/Cu multilayer film in the tropical marine climate, so as to provide reference for the research on the early warning of corrosion failure in electron components. Methods In this study, magne-tron sputtering was used to develop Au/Ni/Cu thin film on p type single crystal Si(100) substrate. The surface and interface struc-ture changes of Au/Ni/Cu thin films in the tropical marine climate were studied using atomic force microscopy ( AFM) and Auger electron spectroscopy ( AES) . Results In the early stage of aging treatment, Au atoms aggregated on the Au/Ni/Cu thin film sur-face and formed discontinuous island structure and micro-cracks around the islands. With the increase of aging time, Ni atoms and Cu atoms diffused to the surface of the Au layer near the corrosion holes formed in the films. As the aging time increased further, the number of the corrosion holes increased, and the corrosion hole area was enlarged, at this time the samples were in the terminal stage of corrosion. In the meantime, no obvious coarsening was observed at the interface of Au/Ni/Cu thin film in the areas away from the corrosion holes. Conclusion The failure of Au/Ni/Cu thin film in tropical marine climate mainly proceeded through sur-face corrosion hole.

参考文献

[1] POATE J M;TU K N;MAYER J W .Thin Films Interdiffu-sion and Reactions[J].Journal of Polymer Science:Poly-mer Letters Edition,1978,17(01):39.
[2] M.I. Danylenko;M. Watanabe;C. Li;A.V. Krajnikov;D.B. Williams;M.A. Vasiliev .Analytical electron microscopy and Auger electron spectroscopy study of low-temperature diffusion in multilayer chromium-copper-nickel-gold thin films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2003(1/2):75-84.
[3] A. Tynkova;S. Sidorenko;S. Voloshko;A.R. Rennie;M.A. Vasylyev.Interdiffusion in Au(120 nm)/Ni(70 nm) thin films at the low-temperature annealing in the different atmospheres[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2013:69-74.
[4] 霍红英,邹敏,马光强,常会.本底真空度对磁控溅射法制备AZO薄膜的影响[J].表面技术,2013(01):75-77.
[5] 徐雪波,贺耀华,贺志勇,鲍明东.非平衡磁控溅射沉积不同成分Ti-Ni合金薄膜的伪弹性研究[J].表面技术,2013(04):28-31.
[6] 严楷;曹江利;姚文清 等.真空环境多场耦合对Au/Cu/Si薄膜界面的影响[J].真空科学与技术学报,2012,33(08):766-770.
[7] Resnik, D;Vrtacnik, D;Aljancic, U;Mozek, M;Zalar, A;Amon, S .Characterization of sputter deposited Au/Ni/Al multilayers on Si substrates[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2009(1):224-227.
[8] Ch. Lang;G. Schmitz .Micro structure-controlled interdiffusion of Cu/Co/Au thin films investigated by three-dimensional atom probe[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):119-125.
[9] M.T. Gudze;R.E. Melchers .Operational Based Corrosion Analysis In Naval Ships[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(12):3296-3307.
[10] MENDOZA A R;CORVO F .Outdoor and Indoor Atmos-pheric Corrosion of Non-ferrous Metals[J].Corrosion Sci-ence,2000,42(07):1123-1147.
[11] Yves Van Ingelgem;Annick Hubin;Jean Vereecken .Investigation of the first stages of the localized corrosion of pure copper combining EIS, FE-SEM and FE-AES[J].Electrochimica Acta,2007(27):7642-7650.
[12] 龚鹏,范真,丁建宁,程广贵,袁宁一,凌智勇.氮化铜薄膜制备中氮气比例对其结构及微观力学性能的影响[J].表面技术,2013(05):15-18,31.
[13] 唐少霞,赵志忠,毕华,谢跟踪.海南岛气候资源特征及其开发利用[J].海南师范大学学报(自然科学版),2008(03):343-346.
[14] 鲁远曙,左卫,王玉龙.海洋性气候电子设备铝合金结构腐蚀防护研究[J].装备环境工程,2008(03):71-75.
[15] M.A. Pech-Canul;P. Castro .Corrosion measurements of steel reinforcement in concrete exposed to a tropical marine atmosphere[J].Cement and Concrete Research,2002(3):491-498.
[16] Properties of Cu film and Ti/Cu film on polyimide prepared by ion beam techniques[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2010(23):P.7010.
[17] Yue He;Jizhong Zhang;Wenqing Yao;Dexing Li;Xu Teng .Effect Of Temperature On Residual Stress And Mechanical Properties Of Ti Films Prepared By Both Ion Implantation And Ion Beam Assisted Deposition[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2009(8):4484-4490.
[18] M. Kawwam;F.H. Alharbi;T. Kayed;A. Aldwayyan;A. Alyamani;N.Tabet;K. Lebbou .Characterization of CuO(111)/MgO(100) films grown under two different PLD backgrounds[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013(Jul.1):7-12.
[19] Louis Scudiero;Ayuba Fasasi;Peter R. Griffiths .Characterization of a controlled electroless deposition of copper thin film on germanium and silicon surfaces[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2011(9):4422-4427.
[20] ISO 18115:2001.Surface Chemical Analysis-Vocabulary[S].
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%