Plastic prestraining was applied to a solder interconnect to introduce internal defects such as dislocations in order to investigate the interaction of dislocations with electromigration damage. Above a critical prestrain, Bi interfacial segregation to the anode, a clear indication of electromigration damage in SnBi solder inter- connect, was effectively prevented. Such an inhibiting effect is apparently contrary to the common notion that dislocations often act as fast diffusion paths. It is suggested that the dislocations introduced by plastic prestraining acted as sinks for vacancies in the early stage of the electromigration process, but as the vacancies accumulated at the dislocations, climb of those dislocations prompted recovery of the deformed samples under current stressing, greatly decreasing the density of dislocation and vacancy in the solder, leading to slower diffusion of Bi atoms.
参考文献
| [1] | Q.L.YANG;J.K.SHANG .Interfacial Segregation of Bi during Current Stressing of Sn-Bi/Cu Solder Interconnect[J].Journal of Electronic Materials,2005(11):1363-1367. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%