采用直流磁控反应溅射法在未加热衬底上沉积TiO2薄膜,以紫外灯为光源进行了薄膜光催化降解亚甲基蓝溶液的实验,研究了沉积工艺参数和后处理退火温度对薄膜光催化性能的影响.结果表明:经过500℃退火、厚度较大的薄膜样品光催化效率较高;膜厚基本相同的样品,沉积时电源功率较小、Ar/O2流量比例较小的薄膜光催化效率较高.
TiO2 thin films were deposited by direct current (DC) magnetron reactive sputtering without external heating. Photocatalytic activity of the samples was tested by degradation of methylene blue solution under irradiation of a UV lamp. The effect of different preparation parameters on photocatalytic activity was investigated. The results show that the thicker film annealed at 500 ℃ has better photocatalytic activity; Thin films deposited with lower source power and lower Ar/O2 flow ratio display better photocatalytic activity when their thicknesses are similar.
参考文献
[1] | Heller Adam .[J].Accounts of Chemical Research,1995,28(12):503-508. |
[2] | Zeman R.;Takabayashi S. .Effect of total and oxygen partial pressures on structure of photocatalytic TiO2 films sputtered on unheated substrate[J].Surface & Coatings Technology,2002(1):93-99. |
[3] | P. Zeman;S. Takabayashi .Nano-scaled photocatalytic TiO_2 thin films prepared by magnetron sputtering[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2003(1/2):57-62. |
[4] | Yamagishi M.;Kuriki S.;Song PK.;Shigesato Y. .Thin film TiO2 photocatalyst deposited by reactive magnetron sputtering[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2003(1/2):227-231. |
[5] | Wang TM.;Zheng SK.;Hao W.;Wang C. .Studies on photocatalytic activity and transmittance spectra of TiO2 thin films prepared by r.f. magnetron sputtering method[J].Surface & Coatings Technology,2002(2/3):141-145. |
[6] | 李海玲,王文静,亢国虎,宋爽,许颖.磁控溅射法制备TiO2薄膜的光催化特性[J].太阳能学报,2006(11):1103-1107. |
[7] | 张玉娟,沈嘉年.TiO2光催化纳米薄膜的晶化处理[J].稀有金属材料与工程,2006(01):92-95. |
[8] | Takeda S;Suzuki S;Odaka H;Hosono H.Photocatalytic TiO2 Thin Films Deposited onto Glass by DC Magnetron Sputtering[A].,2000:707. |
[9] | Zhang Y X;Shen J;Yang X L et al.Influence of Deposition Rate and Relative Parameters on Properties of TiO2 Thin Films Prepared by DC Reactive Magnetron Sputtering[J].Journal of Vacuum Science and Technology,2000,20:13-18. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%