采用机械合金化法制备了Mg65Cu25Gd10非晶粉末,并研究了球磨的转速、球料比和球磨时间等工艺参数对非晶形成的影响.研究表明当球料比为20∶1,转速为200r/min时较为合适,形成非晶所需的最短时间为40h.采用差示扫描量热仪(DSC)研究了球磨得到的非晶粉末的热稳定性,得到了热力学参数玻璃转化温度Tg、开始晶化温度Tx,过冷液相区宽度ΔTx和晶化焓ΔH等,并将其与熔炼法获得的样品进行对比,发现其热力学参数不受工艺过程的影响,仍然具有很好的热稳定性.同时,用Kissinger方程式对非晶粉末的晶化动力学进行了计算,得到了Tg和Tx的表观激活能.
参考文献
| [1] | Pryds N H .Bulk amorphous Mg-based alloys[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,375-377:186. |
| [2] | 孙琴,陈刚,王宁,李宝贵,张伟.Mg-Cu-Y块体金属玻璃的塑性变形特性[J].热加工工艺,2005(04):56-57,72. |
| [3] | 黎业生,吴子平,刘赣伟,陈辉惶.镁基大块金属玻璃的制备及研究进展[J].铸造,2005(08):745-748. |
| [4] | Park ES;Lee JY;Kim DH .Effect of Ag addition on the improvement of glass-forming ability and plasticity of Mg-Cu-Gd bulk metallic glass[J].Journal of Materials Research,2005(9):2379-2385. |
| [5] | Yuan Guangyin;Inoue Akihisa .The effect of Ni substitution on the glass-forming ability and mechanical properties of Mg-Cu-Gd metallic glass alloys[J].Journal of Alloys and Compounds,2005,387:134. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%