采用间歇式超临界水氧化装置，对316L不锈钢网状试样和块状试样在超临界水氧化处理城市污泥环境中的腐蚀特性进行了研究。结果表明，试样的腐蚀程度随氧化系数的提高而加剧，碱性条件下网状试样表面有富含Mo和Ni的丝状无机盐生成。与网状试样不同，块状试样在高氧化系数和酸性条件下均表现出点蚀形貌，在酸性条件下腐蚀速率最高达0．17mm／a，经历高氧化系数（2．0）、酸性（pH=5．2）和碱性（pH=10．05）条件下分别腐蚀10h后，块状试样表面呈现点蚀形貌，表层氧化物主要为Fe3O4-NiFe2O4。
The corrosion behavior of 316L stainless steel netlike and block samples was studied in city sewage sludge treated by supercritical water oxidation （SCWO）. The results showed that the corrosion of 316L was enhanced as the oxidation coefficient increased. Filament mineral salts rich in Mo and Ni were found on the outer surface of the net like sample under alkaline condition. Different from the net like sample, on the block sample pitting corrosion morphology was observed under the acidity and high oxidation conditions. 316L had the highest corrosion rate of 0.17 mm/a under the acid SCWO condition. The surface oxide on the block sample was mainly Fe3O4-NiFe2O4 and pitting corrosion was observed under the testing conditions of high oxidation coefficient （2. 0）, acidity （pH=5.2） and alkalinity （pH=10. 05） for 10 h.
参考文献
| [1] | 贺文智,李光明,孔令照,赵修华,王华,黄菊文.基于腐蚀与盐堵塞问题的超临界水氧化研究进展[J].环境工程学报,2007(05):1-6. |
| [2] | Tina M.Hayward;Igor M.Svishchev;Ramesh C.Makhija .Stainless steel flow reactor for supercritical water oxidation:corrosion tests[J].The Journal of Supercritical Fluids,2003(3):275-281. |
| [3] | Noam Eliaz;D. Bryce Mitton;Ronald M. Latanision .REVIEW OF MATERIALS ISSUES IN SUPERCRITICAL WATER OXIDATION SYSTEMS AND THE NEED FOR CORROSION CONTROL[J].Transactions of the Indian Institute of Metals,2003(3):305-314. |
| [4] | Peter Kritzer .Corrosion in high-temperature and supercritical water and aqueous solutions: a review[J].The Journal of Supercritical Fluids,2004(1/2):1-29. |
| [5] | M.D.Bermejo;F.Fdez-Polanco;M.J.Cocero .Experimental study of the operational parameters of a transpiring wall reactor for supercritical water oxidation[J].The Journal of Supercritical Fluids,2006(1):70-79. |
| [6] | Bermejo MD;Fdez-Polanco F;Cocero MJ .Effect of the transpiring wall on the behavior of a supercritical water oxidation reactor: Modeling and experimental results[J].Industrial & Engineering Chemistry Research,2006(10):3438-3446. |
| [7] | 马承愚,姜安玺,彭英利,李芬,闫波.含氯介质超临界水氧化过程中几种镍基合金腐蚀的实验研究[J].过程工程学报,2006(01):124-127. |
| [8] | 朱发文,张乐福,唐睿,乔培鹏,刘瑞芹.奥氏体304NG不锈钢在550℃/25 MPa超临界水中的腐蚀行为[J].原子能科学技术,2009(06):518-522. |
| [9] | 卢建树,王保峰,张九渊,毛志远.几种合金在超临界水氧化苯酚中的腐蚀[J].材料研究学报,2002(01):41-45. |
| [10] | R. Fujisawa;M. Sakaihara;Y. Kurata .Corrosion behaviour of nickel base alloys and 316 stainless steel in supercritical water under alkaline conditions[J].Corrosion Engineering, Science and Technology,2005(3):244-248. |
| [11] | Son SH;Lee JH;Byeon SH;Lee CH .Surface chemical analysis of corroded alloys in subcritical and supercritical water oxidation of 2-chlorophenol in continuous anticorrosive reactor system[J].Industrial & Engineering Chemistry Research,2008(7):2265-2272. |
| [12] | 张丽,韩恩厚,柯伟.GH132管在超临界水氧化反应法处理航天推进废水环境中的腐蚀[J].中国腐蚀与防护学报,2004(02):121-124. |
| [13] | 卢建树,李肖华,张九渊,邹金桥.316不锈钢和825镍基合金在超临界水氧化毒死蜱介质中的腐蚀[J].腐蚀科学与防护技术,2002(04):187-190. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%