The diffusion of La in ε-Fe2～3N(ε)and γ′-Fe4N (γ′)phases pro duced by plasma nitriding was studied. It is found that with increasing nitridin g time, the ε phase continuously decomposes into γ′ one under employed experi mental conditions and compared with γ′ phase or ε+γ′ ones, the mono one ε has an impedient effect on depth of La diffusion. The growth of La layer in dua l phases and mono one follows an approximate exponential law and a parabolic one , respectively, and this kinetics law does not change with increasing temperatur e. The effect of increasing temperature in the range of 520 to 560 ℃ on La d iffusion depth is less than that of phase constitution change such as the decomp osition of ε phase into γ′ one.
参考文献
| [1] | Wei Yongde;Liu Zhiru;Wang Chunyi et al.A note on coating o f surface diffusion infiltration of RE on steel 20 and armco iron by chemical pr ocess[J].金属学报,1983,19(05):B197. |
| [2] | Wei Yongde;Liu Zhiru;Wang Chunyi .Effect of rare earth ele ments on surface activating and micro-alloying of carbonitriding process and it s application[J].Journal of Rare Earths(in Chinese),1986,4(01):47. |
| [3] | Liu Zhiru;Chen Yang;GUO Yi.Effect of rare earth element La on the n itrocarburizing kinetics microstructure and properties of steel 20[J].Heat Treatment of Metals(in Chinese),1989(07):13. |
| [4] | Sun Y;Li X;Bell T .Low temperature plasma carburizing of austenitic stainless steels for improved wear and corrosion resistance[J].Surface Engineering,1999,15(01):49. |
| [5] | Crank J.The Mathematics of Diffusion[M].Oxford:Clarendon Pres s,1975 Bibliography of Science and Technology of Rare EarthsPublished in China,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%