Age hardening in Cu-3.2Ni-0.75Si (wt pct) and Cu-1.0Ni-0.25Si (wt pct) alloys from 723 to 823 K is studied. After an incubation period strengthening appears which is due to precipitates in the Cu-1.0Ni-0.25Si (wt pct) alloy. On other hand animmediate increase of the yield strength characterizes the aging of the alloy. This is followed by the regions of constant yield strength and further by a peak. The microstructure of the alloy was studied by, means of transmission electron microscope (TEM) and X-ray diffraction (XRD). Spinodal decomposition takes place followed by nucleation of the ordering coherent (Cu,Ni)3Si particles, further precipitation annealing coherent δ-Ni2Si nucleated within the (Cu,Ni)3Si particle. Any change of the yield strength can be described by an adequate change of the structure in the sample. The nature of the aging curves with a"plateau" is discussed. The formulas of Ashby and Labusch can be used to explain the precipitation.
参考文献
| [1] | P. LIU;B. X. KANG;X. G. CAO .Strengthening mechanisms in a rapidly solidified and aged Cu-Cr alloy[J].Journal of Materials Science,2000(7):1691-1694. |
| [2] | P Liu;B X Kang;X G Cao;J.L.Huang B.Yen and H.C.Gu .[J].Materials Science and Engineering,1999,265:262. |
| [3] | H Fernee;J Nairn;A Atrens .[J].Journal of Materials Science,2001,36:2711. |
| [4] | H J Ryu;H K Baik;S H Hong .[J].Journal of Materials Science,2000,35:3641. |
| [5] | S A Lockyer;F W Noble .[J].Journal of Materials Science,1994,29:218. |
| [6] | Hidemichi Fujiwara;Tatsuo Sato;Akihiko Kamio .[J].Journal of the Japan Institute of Metals,1998,62(04):301. |
| [7] | Rensei Futatsuka .[J].Journal of the Japan Copper and Brass Research Association,1997,36:25. |
| [8] | J.-C.Zhao;M.R.Notis .Spinodal decomposition, ordering transformation, and discontinuous precipitation in a Cu-15Ni-8Sn alloy[J].Acta materialia,1998(12):4203-4218. |
| [9] | S A Lockyer;F W Noble .[J].Materials Science and Technology,1999,15(10) |
| [10] | P Kratochvil;J Mencl;J Pesicka;S.N.Kominik .[J].Acta Materialia,1984,32(09):1493. |
| [11] | D E Laughlin;J W Cahn .[J].Acta Materialia,1975,23(03):329. |
| [12] | A Datta;W A Soffa .[J].Acta Materialia,1976,24:987. |
| [13] | P E Donovan;A W Thompson .[J].Journal of Materials Science,1989,24:756. |
| [14] | A W Thompson;J C Williams .[J].METALL,1984,15(05):931. |
| [15] | M F Ashby;Y.In.Oxide Dispersion Strengthening[M].Gordon and Breach, New York,1958:143. |
| [16] | T Gadman .[J].Materials Science and Technology,1999,15(01):30. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%