A detailed study has been carried out to investigate the effect of applied current density on the composition, crystallographic structure, grain size, and surface morphology of Fe-Cu films. X-ray diffraction (XRD) results show that the films consist of a mixture of face-centered cubic (fcc) Cu and body centered cubic (bcc) ~-Fe phases. The average crystalline size of both Fe and Cu particles decreases as the applied current density becomes more negative. Compositional analysis of Fe-Cu films indicates that the Fe content within the films increases with decreasing current density towards more negative values. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) have been used to investigate the surface morphology of Fe-Cu films. It is observed that the surface morphology of the films changes from dendritic structure to a cauliflower structure as the applied current density becomes more negative. The surface roughness and grain size of the Fe-Cu films decrease with decreasing applied current density towards more negative values.
参考文献
| [1] | S.S. El-Egamy .Corrosion and corrosion inhibition of Cu-20%Fe alloy in sodium chloride solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(4):928-937. |
| [2] | M. K. Roy;H. C. Verma .Mossbauer studies of Fe-Cu alloys prepared by electrodeposition[J].Journal of Magnetism and Magnetic Materials,2004(1/2):186-193. |
| [3] | S. K. Ghosh;A. K. Grover;G. K. Dey;M. K. Totlani .Nanocrystalline Ni-Cu alloy plating by pulse electrolysis[J].Surface & Coatings Technology,2000(1):48-63. |
| [4] | S. H. Kim;U. Erb;K. T. Aust .The Corrosion Behavior Of Nanocrystalline Electrodeposits[J].Plating & Surface Finishing,2004(5):68-70. |
| [5] | E. Budevski;G. Staikov;W. J. Lorenz .Electrocrystallization nucleation and growth phenomena[J].Electrochimica Acta,2000(15/16):2559-2574. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%