以慢速率拉伸試驗来評估硫化應力腐蝕,對於時效PH13-8Mo不銹鋼,其缺口拉伸强度(NTS)以及拉伸破壞特征的影響,實驗并利用電化學滲透方法来測定不同顯微組織其氫擴散速率、氫通量以及视固溶量.實驗結果顯示:所有時效試片對於硫化應力腐蝕皆展現出高程度敏感性.氫滲透結果指出,H800、H900以及H1000時效試片具有極爲相近的氫滲特性,然而相對於其他試片,H1100試片却表現出較低的氫擴散率、氫通量以及較高的固溶量.當試片時效温度低於1000°F時,類同的氫滲性質導致不同試片具有相同程度的氫脆敏感性,而H1100試片顯現相對較低的氫脆性.當試片時效温度低於1000°F時,氫被捕集在基地中而呈現準劈裂破壞的特征.此外,在H1100試片中由於存在着晶界沃斯田鐵,氫趨向於沿着晶界擴散并被捕集,造成試片在應變過程中産生了些許沿晶破壞.
参考文献
| [1] | SeetharamanV;Sundararaman M;Krishnan R .[J].Materials Science and Engineering,1981,47(01):1. |
| [2] | [J].Metallurgical and Materials Transactions,1994,25A(04):789. |
| [3] | MunnP;erssonB .[J].Corrosion Science,1990,46(04):286. |
| [4] | HochanadelPW;Robino C V et al.[J].Metallurgical and Materials Transactions,1994,25(04):697. |
| [5] | MurryGT;Honegger H H;Mousel T .[J].Corrosion,1984,40(04):146. |
| [6] | YoungLM;Eggleston M R et al.[J].Materials Science and Engineering,1995,203(1-2):377. |
| [7] | ScullyJR;Cieslak M J et al.[J].Scripta Materialia,1994,31(02):125. |
| [8] | GaughRR .Armco Steel Corporation,Baltimore and Maryland[J].Materials Performance,1977,16(09):24. |
| [9] | DevanathanMA;Stachurski Z .[J].Proc Roy Sic London,1962,270:90. |
| [10] | ValentiniR;Solina A .[J].Materials Science and Technology,1994(10):908. |
| [11] | XuJ;Yuan X Z;Sun X K et al.[J].Scripta Materialia,1993,29:925. |
| [12] | ParvathavarthiniN;Saroja S;Dayal R K .[J].Journal of Nuclear Materials,1999,264:35. |
| [13] | ToriioJ;Lancha A M;Elices M .[J].Materials Science and Engineering,1991,145(02):167. |
| [14] | ToriioJ .[J].Journal of Materials Science,1993,28(09):2289. |
| [15] | YokooriJrAT;Nemoto T;Satoh K et al.[J].Engineering Fracture Mechanics,1996,55(01):47. |
| [16] | HardieD;Su′e Liu .[J].Corrosion Science,1996,38(05):721. |
| [17] | SuLiu;Zhu Ziyong;Ke Wei .[J].Journal of Materials Science and Technology,1994,12(01):51. |
| [18] | PressouyreGM;Bernstein I M .[J].Acta Materialia,1979,27(01):89. |
| [19] | PressouyreGM;Bernstein I M .[J].Metallurgical and Materials Transactions,1978,9(11):157. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%