用扫描电镜结合粒度分析方法,研究几种不同生产方法聚氯乙烯(PVC)糊树脂颗粒形态及其对增塑糊黏度性能的影响.结果表明,颗粒表面圆整,具有双峰粒度分布、次级粒子聚集松散的微悬浮法糊树脂所制增塑糊黏度最低,在1240 mPa·s～1390 InPa·s之间;其次是种子微悬浮法增塑糊;再次为种子乳液法增塑糊;颗粒形状不规则且表面粗糙,具有双峰粒度分布、次级粒子聚集较紧密的混合法增塑糊黏度最高,在1820 mPa·s～3050 mPa·s之间.对于增塑糊的存放稳定性,种子微悬浮法的效果最好,黏度变化率在6%以下;其次是微悬浮法和种子乳液法;混合法的最差,黏度变化率在41%以上.
参考文献
| [1] | 吉玉碧,徐国敏,张敏敏,胡智,杨二铆,谭红.PVC增塑糊黏度及其稳定性正交实验研揪[J].塑料工业,2009(01):45-48,52. |
| [2] | N.Nakajima;E.R.Harrell .Rheology of PVC Plastisol: Particle Size Distribution and Viscoelastic Properties[J].Journal of Colloid and Interface Science,2001(1):105-115. |
| [3] | Marcilla A;Garcia JC;Beltran M .Study of the flow properties and the ageing process in PVC plastisols from commercial PVC resins[J].European Polymer Journal,1997(5):753-759. |
| [4] | Makarewicz E.;Janczak K. .The influence of structure parameters and property of surface-active agents on stability of water dispersions of PVC plastisol [Review][J].Progress in Organic Coatings: An International Review Journal,2004(2):165-179. |
| [5] | 蒋宜捷,施立群.聚氯乙烯糊树脂颗粒形态与增塑糊性能关系的研究[J].聚氯乙烯,2001(02):14-16. |
| [6] | 蒋宜捷.激光衍射散射式测粒技术在聚氯乙烯糊树脂粒径分析中的应用[J].聚氯乙烯,2006(06):32-35. |
| [7] | 吉玉碧,徐国敏,张敏敏,胡智,罗恒,杨一钘,陆洋,谭红.PVC糊树脂颗粒形态研究[J].塑料科技,2009(09):23-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%