采用微弧氧化技术在AZ31B镁合金表面制备陶瓷层,利用其表面多孔结构借助电泳技术沉积有机膜层,对比研究陶瓷层和复合膜层表面粗糙度、表面及截面形貌、电化学性能及划伤腐蚀特性.结果表明:陶瓷层表面放电微孔被电泳层完全填充并形成均匀膜层,复合膜层表面粗糙度明显降低;微弧电泳复合膜层腐蚀电流密度与陶瓷层和基体相比分别降低2个和4个数量级,极化电阻分别增大2个和4个数量级,腐蚀倾向降低;微弧电泳复合膜层电化学阻值与陶瓷层相比增加4个数量级,同时电容值降低4个数量级,耐蚀性显著提高;由于陶瓷层与电泳层的机械嵌合作用,复合膜层划伤腐蚀过程表现为基体腐蚀及陶瓷层与基体界面的破坏,复合膜层界面处结合完好.
参考文献
| [1] | 倪军,刘榕芳,肖秀峰.电泳沉积HA/Ti复合涂层的结合强度和热稳定性[J].稀有金属材料与工程,2006(01):119-122. |
| [2] | Song, G.-L. .A dipping E-coating for Mg alloys[J].Progress in Organic Coatings: An International Review Journal,2011(4):252-258. |
| [3] | Hu, R.-G.;Zhang, S.;Bu, J.-F.;Lin, C.-J.;Song, G.-L. .Recent progress in corrosion protection of magnesium alloys by organic coatings[J].Progress in Organic Coatings: An International Review Journal,2012(2/3):129-141. |
| [4] | 崔学军,周吉学,林修洲,罗宏,龚敏.镁合金AZ31锰系磷化膜的生长过程及形成机理[J].中国有色金属学报,2012(01):15-21. |
| [5] | Zhang, J;Wu, CY .Corrosion protection behavior of AZ31 magnesium alloy with cathodic electrophoretic coating pretreated by silane[J].Progress in Organic Coatings: An International Review Journal,2009(4):387-392. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%