采用双环电化学动电位再活化法(EPR)对敏化处理后的304不锈钢试样进行晶间腐蚀试验,然后采用金相法观察试验后试样表面优先腐蚀的贫铬区的形态特征.结果表明,304不锈钢在敏化过程中,贫铬区首先以点状分布于晶界附近,随着敏化程度的加剧,贫铬区不断扩展连接,形成链状分布,链状的贫铬区再发生交联,最终以网状分布于晶界附近.
参考文献
| [1] | M. Terada;D.M. Escriba;I. Costa .Investigation on the intergranular corrosion resistance of the AISI 316L(N) stainless steel after long time creep testing at 600 deg C[J].Materials Characterization,2008(6):663-668. |
| [2] | Sandip Ghosh Chowdhury;Raghuvir Singh .The influence of recrystallized structure and texture on the sensitization behaviour of a stable austenitic stainless steel (AISI 316L)[J].Scripta materialia,2008(12):1102-1105. |
| [3] | A. Yae Kina;V.M. Souza;S.S.M. Tavares .Microstructure and intergranular corrosion resistance evaluation of AISI 304 steel for high temperature service[J].Materials Characterization,2008(5):651-655. |
| [4] | H. SIDHOM;T. AMADOU;H. SAHLAOUI .Quantitative Evaluation of Aged AISI 316L Stainless Steel Sensitization to Intergranular Corrosion: Comparison Between Microstructural Electrochemical and Analytical Methods[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2007(6):1269-1280. |
| [5] | Kenji Kaneko;Tatsuya Fukunaga;Kazuhiro Yamada .Formation of M_(23)C_6-type precipitates and chromium-depleted zones in austenite stainless steel[J].Scripta materialia,2011(6):509-512. |
| [6] | 罗宏,龚敏.奥氏体不锈钢的晶间腐蚀[J].腐蚀科学与防护技术,2006(05):357-360. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%