研究了Mg-8Al-Sr-xCa合金的显微组织和力学性能.铸态合金组织主要由α-Mg相和β-Mg17Al12相组成.在Ca添加至1.5％(质量分数,下同)后,形成少量Al2Ca颗粒.挤压过程中合金发生了动态再结晶,晶粒明显细化,同时第二相碎化,时效后组织中的β相趋于球形.拉伸结果显示,在Ca含量由0.5％增至1.5％时,铸态和挤压时效态合金的拉伸性能逐渐提高.挤压时效态AJ80+1.5％Ca的屈服强度和抗拉强度分别为274 MPa和327 MPa,该合金优异的拉伸强度主要是细晶强化和Al2Ca颗粒与含Ca的β-Mg17Al12相析出强化的结果.
参考文献
| [1] | 杜文博,吴玉锋,聂祚仁,苏学宽,左铁镛.稀（碱）土在镁合金中的作用及应用现状[J].稀有金属材料与工程,2006(09):1345-1349. |
| [2] | Hirai K;Somekawa H;Takigawa Y;Higashi K .Effects of Ca and Sr addition on mechanical properties of a cast AZ91 magnesium alloy at room and elevated temperature[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):276-280. |
| [3] | 张新明,彭卓凯,陈健美,邓运来.耐热镁合金及其研究进展[J].中国有色金属学报,2004(09):1443-1450. |
| [4] | Liang, SM;Chen, RS;Blandin, JJ;Suery, M;Han, EH .Thermal analysis and solidification pathways of Mg-Al-Ca system alloys[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1-2):365-372. |
| [5] | 曾小勤,王渠东,吕宜振,丁文江,朱燕萍,翟春泉,卢晨.Mg-9Al-0.5Zn-0.1Be-XCa合金的组织和力学性能研究[J].机械工程材料,2001(05):15-18. |
| [6] | 汤振雷,王为.计算合金系统热力学性质的Miedema模型的发展[J].材料导报,2008(03):115-118. |
| [7] | 孙顺平,易丹青,臧冰.基于Miedema模型和Toop模型的Al-Si-Er合金热力学参数计算[J].稀有金属材料与工程,2010(11):1974-1978. |
| [8] | 唐建成,黄伯云,贺跃辉,刘文胜,周科朝.Ti-Al基合金中的Hall-Petch关系及影响因素分析[J].金属学报,2002(04):365-368. |
| [9] | 郑宏伟,唐荻,武会宾,杨柳.控轧控冷工艺对X120管线钢碳氮化物析出的影响[J].华南理工大学学报（自然科学版）,2012(07):128-134. |
| [10] | 贾淑果,刘平,任凤章,田保红,郑茂盛,周根树.高强高导低溶质Cu-Ag-Cr合金时效析出特性的研究[J].材料热处理学报,2004(02):8-10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%