在实验室条件下试制800 MPa级低硅热镀锌双相钢,研究了双相钢的双相处理工艺、组织和性能.实验结果表明:试样组织为铁素体+马氏体的双相组织,M的体积含量是15%～20%.通过三种不同的热处理温度获得了不同的F+M的比例,从而得到不同的力学性能.退火温度从780℃升到850℃,可以获得性能更好的双相钢.
参考文献
| [1] | Irie T;Satoh S;Hashigushi K.Affecting the Formability of Cold-rolled High Strength Steel Sheets[J].Transactions of the Iron and Steel Institute of Japan,1981(21):793. |
| [2] | Furukawa T;Morikawa H;Endo M.Hot Rolled High Strengh Steel Sheet for Automotive Use Produced by Controlled Cooling[J].Trans.ISU,1981(21):812. |
| [3] | Abe M;Takeshi H.Manufacturing Techniques for High Strength Steel Sheets for Automotive Applications[J].Nippon Steel Tech Rep,1984(23):9. |
| [4] | 马鸣图;吴宝榕.双相钢-物理和力学冶金[M].北京:冶金工业出版社,1988 |
| [5] | Debanshu Bhattacharya.Developments in Advanced High Strength Steels[J].Iron& Steel Supplement,2005(40):69. |
| [6] | Akihiko Nishimoto.Influence of Alloying Elements in Hot Dip Galvanized High Tensile Strength Sheet Steels on the Adhesion and Iron-zinc Alloying Rate[J].Tetsu-to-Hagane,1982(68):278. |
| [7] | 邝霜,康永林,于浩,窦婷婷,尹显东,刘仁东.600MPa级冷轧双相钢的试制与研究[J].材料工程,2006(z1):329-333. |
| [8] | 姜锡山.特殊钢缺陷分析与对策[M].北京:化学工业出版社,2006 |
| [9] | 朱晓东,王利.连续退火工艺参数对Si-Mn系冷轧双相钢的力学性能的影响[C].2003中国钢铁年会论文集,2003:2571-2575. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%