制备了不同Y含量的Mg-5A1-1Sr-2Ca-xY（x=0，1，2，5）合金试样，采用光学显微镜（OM）、扫描电子显微镜（SEM）、X射线衍射仪（XRD）、材料试验机等观察测试合金的微观组织和力学性能。结果表明，未添加Y时，合金晶粒大小不均匀，且多呈柱状，晶内有较多的点状化合物；Y含量1％时，晶粒细化、球化且大小较均匀；Y含量2％时，晶粒趋于柱状；Y含量5％时，晶粒形状不规则、大小极不均匀。随Y含量的增加，室温和高温力学性能呈先升后降趋势，最高点为Y含量1％，其室温和高温抗拉强度分别较无Y合金提高了约33．8％和25．4％。
Mg-5Al-lSr-2Ca-xY （x = 0 -5 ）magnesium alloys were melted in a grabhite crucible furnace under argon atmosphere. Microstructure and mechanical properties of the alloys were examined by means of metallographic microscope, SEM, XRD and tensile tests. The results show that when Y addition is 1% , the grain size is refined and more uniform with spheroidal shape, while without Y addition, the alloys present irregular columnar grains with spotshaped compounds. When Y addition is 2 % , the alloy presents fine columnar grains, and the nonuniform and irregular grains are observed in the alloy with addition of 5% yttrium. When the Y addition is 1% , tensile strength of the alloy at ambient and elevated temperature is improved by 33.8% and 25.4% compared with that of the alloy without Y addition, however, with the Y addition of 2% -5 % , the tensile properties of the alloys decrease obviously.
参考文献
| [1] | A. A. Luo .Recent magnesium alloy development for elevated temperature applications[J].International Materials Reviews,2004(1):13-30. |
| [2] | 张忠明,徐春杰,贾树卓,郭学锋.高硅含量镁铝硅合金的组织与力学性能[J].材料热处理学报,2009(05):140-144. |
| [3] | 刘宏伟,罗承萍,刘江文.钇及混合稀土对AZ91镁合金时效析出的影响[J].机械工程材料,2004(04):29-32. |
| [4] | Bai Jing;Sun Yangshan;Xun Shan;Xue Feng;Zhu Tianbai .Microstructure and tensile creep behavior of Mg-4Al based magnesium alloys with alkaline-earth elements Sr and Ca additions[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):181-188. |
| [5] | ALAN A. LUO;MICHAEL P BALOGH;BOB R. POWELL .Creep and Microstructure of Magnesium-Aluminum-Calcium Based Alloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2002(3):567-574. |
| [6] | 李全安,李建弘,谢建昌,李克杰,张兴渊.含钇Mg-6Al镁合金组织和高温力学性能[J].材料热处理学报,2009(03):127-131. |
| [7] | R. Wu;C. Wang;M. Zhang .Behaviour of calcium in Mg-6Li-3Al alloy[J].Kovove materialy,2009(3):169-174. |
| [8] | 黄晓锋,周宏,何镇明.Structure Analysis of Oxidation Film of Ignition-Inhibition AZ91D Ma gnesium Alloy Added with Cerium[J].稀土学报(英文版),2003(01):73-76. |
| [9] | 李金锋,耿浩然,杨中喜,王英姿,崔峰,孙春静.钇对AZ91镁合金组织和力学性能的影响[J].铸造,2005(01):53-56. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%