综述了钛生物医学材料在体液中的耐蚀性能.主要阐述了局部腐蚀、磨损腐蚀、腐蚀疲劳和应力腐蚀破裂等4种腐蚀形式.进而展望了目前钛生物材料的研究动向及应用前景.
The corrosion resistance of Ti biomedical materials in body fluids was reviewed. The main corrosion types including local corrosion, fretting corrosion, corrosion fatigue and stress corrosion cracking were introduced. It was showed that the titanium and t
参考文献
| [1] | 三浦维四．医疗用钛手册．日本钛协会,1992,6362FrakerAC,RufAW,SungP,VanOrdenAC,SpeckKM．ASTM．STP,1981,7963GrifinCharlesD,BuchananRA,LemonsJE．J．Biomed．Mat．Res．,1983,17:4894HoarTP,MearsDC．Proc．Roy．Soc．1966,4865GalanteJ,RostokerW．Clin．Orthop．andRelat．Res．,1972,86:2376SesetaN．整形外科MOOK,1986,8:4517MckelopH,KirkpatrickJ,MarkolfK,AmstutzH．Trans．Orthop．Res．Soc．,1980,5:968JohnTScales．J．BoneJointSurg．[Br],1991,73B:5349BuchananRA,BaconRK,WiliamsJM,BeardsleyGM．Trans．Soc．Biomat．,1983,VI:10610MuchaA,BraunM．SurfaceandCoatingsTechnology,1992,50:13511BuchananRA,RigeyED,WiliamsJM．J．Biomed．Mat．Res．,1987,21:35512HarthGH．MetalImplantsforOrthopedicandDentalSurgery．MCICReport//February1974,125913TitaniumAloysinSurgicalImplants．Ed．byluckey//kubliASTMSpecialTechnicalPublication,1983,79614BechtolCO,FergusonAB,LaingPG．MetalsandEngineeringinBoneandJointSurgery．WiliamsandWilkings,Baltmore1959,37915DobbsHS,RobertsonJIM．EngineeringinMedicine,1982,11(4):17516ImamMA．ASTMSTP,1979,68417BlackburnMJ,FeeneyJA,BeckTR．Adv．Coros．Sci．Technol,1973,3:6718SemlitschM,StaubF,WeberH．Biomed．Technik,1985,30:33419BundyKJ,MarekM,HochmanRF．J．Biomed．Mater．Res．,1983,17:46720BremeJ,HeimkeG．Titanium'84Sci．andTech．,1980,32721LuckeyTD,VenugopalB．Metaltoxicityinmammals．NewYorketc:PlenumPress,1977,122MacdonaldTL,HumphreysWG,MartinRB．Science,1987,236:18323YOkazaki,YIto,AItoandTTateishi．J．JapanInst．Metals,1993,57(3):33224WangK,GustavsonL,DumbletonJ．TheMinerals,MetalsandMaterialsSoc．,1993,425梁成浩,杨大智．北京科技大学学报,1996,18(增刊):126梁成浩．表面技术,1997,26(2):15 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%