利用DSC研究了不同结晶速率下四种具有不同乙烯含量的抗冲共聚聚丙烯的非等温结晶动力学,采用Avrami方程和Avrami-Ozawa方程的结合(莫氏法)分析了非等温结晶动力学,结果表明,四种样品的Avrami指数在5～6范围内,说明具有不同乙烯含量的四种样品中的PP的结晶方式并不随冷却速率的变化而变化.F(T)的值随结晶度的增加而增加,a的值也有相似的变化,但变化不大,表明冷却速率越快,在单位时间内的结晶度越大,结晶方式并无多大变化.
参考文献
| [1] | Yang D C;Zhang B L;Yang Y K et al.[J].Polymer Engineering and Science,1984,24:612-617. |
| [2] | Jang B;Uhlmann D R;Vander Sands J B .[J].Journal of Applied Polymer Science,1985,30:2485-2504. |
| [3] | Van Gisbergen J G M;Hoeben W F L M;Meiger H E H .[J].Polymer,1991,31:1539-1544. |
| [4] | Choudhary V;Varma H S;Varma I K .[J].POLYMER,1991,32:2541-2545. |
| [5] | D′Orazio L;Mancarella C;Martuscelli E et al.[J].Polymer,1993,34:3671-3681. |
| [6] | Chiang W;Yang W D;Pukanszky Bela .[J].Polymer Engineering and Science,1992,32:641-648. |
| [7] | D′Orazio L;Mancarella C;Martuscelli E .[J].POLYMER,1991,32:1186-1194. |
| [8] | Prentici P;Williams J G .[J].Plastics And Rubber Processing And Applications,1982,2:27-32. |
| [9] | Sun D;Yu F S;Qi Y C.[J].Polym Acad,1991(02):142-146. |
| [10] | Bartczak;Galeski A;Martuscelli E et al.[J].Polymer,1985,26:1843-1848. |
| [11] | Ven Ser Van der.Polypropylene and Other Polyolefins[M].Els.Sci.Pub B.V,1990:134. |
| [12] | Mirabella F M .[J].Polymer,1993,348:1729-1735. |
| [13] | Moore E O.Polypropylene Handbook[M].Hanser Publishers Munich,1996:92. |
| [14] | Sano H;Usami T;Nakagawa H.[J].Polymer,1986(2710):1497-1504. |
| [15] | Usami T;Gotoh Y;Umemoto H et al.[J].Journal of Applied Polymer Science,1993,52:145-158. |
| [16] | Avrami M .[J].J Chem Phys,1939,7:1103-1112. |
| [17] | Avrami M .[J].J Chem Phys,1940,8:212-224. |
| [18] | Ozawa T .[J].Polymer,1971,12:150-158. |
| [19] | Liu T;Mo Z .[J].Polymer Engineering and Science,1997,37:568-575. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%